Preparation of high molecular weight polymers by direct arylation and heteroarylation

ABSTRACT

A method for preparing polymers by direct heteroarylation or arylation polycondensation is described herein. The method includes preparing a reaction mixture including at least a monomer to be polymerized, a catalyst and a ligand; heating the reaction mixture; and, optionally, end-capping the reaction mixture.

CROSS-REFERENCE TO RELATED APPLICATIONS

The present application is a divisional of co-pending U.S. patentapplication Ser. No. 14/352,541, filed Apr. 17, 2014, which is anational phase application under 35 U.S.C. §371 of InternationalApplication No. PCT/CA2012/000970, filed Oct. 22, 2012, which thebenefit of priority from U.S. Provisional Application No. 61/549,478,filed Oct. 20, 2011, U.S. Provisional Application No. 61/576,045, filedDec. 15, 2011 and U.S. Provisional Application No. 61/651,915, filed May25, 2012, the contents of which are incorporated herein by reference intheir entirety.

FIELD

The present disclosure broadly relates to methods for the synthesis ofpolymers via direct arylation and heteroarylation. More specifically,but not exclusively, the present disclosure relates to the synthesis ofheteroaryl polymers via direct arylation and heteroarylation.

BACKGROUND

The last several years have witnessed significant advances in the fieldof plastic electronics (i.e. light-emitting diodes, photovoltaicdevices, biosensors, etc.). The availability of simple and reliablecoupling procedures (i.e. Stille, Suzuki, Heck, Kumada, etc.) to affordwell-defined and reproducible polymeric materials is directly linked tothe many advances in the field of plastic electrodes. However, thesestate-of-the-art methods generally involve organometallic reagents whichcreate metal waste and require additional synthetic steps and moreextensive purification procedures.

The Stille cross-coupling reaction has allowed significant advances inthe synthesis of new organic molecules.^([1]) This reaction also had asignificant impact in the field of macromolecular chemistry, especiallyregarding the synthesis of conjugated polymers.^([1,2]) However,notwithstanding its great versatility, the Stille reaction involvesdrawbacks such as the formation of toxic tin by-products and in somecases, instability of the organometallic reagents.

Recently, the development of reactions called “direct arylation” hasreceived much attention.^([3]) These reactions allow the formation ofcarbon-carbon bonds between aromatics units with activated hydrogenatoms without the use of organometallic intermediates. Actually, thesereactions are mostly developed for the synthesis of smallmolecules.^([4]) Indeed, up to now, only a few publications reported theuse of direct arylation in polymerization reactions.^([5]) Moreover,there are very few examples showing the coupling between thiophenes orthiophene derivatives via direct heteroarylation and these moieties areparticularly important monomers for plastic electronics.

The thieno[3,4-c]pyrrole-4,6-dione (TPD) unit is a useful building blockfor the development of new conjugated polymers for organic solar cells(power conversion efficiencies up to 7.3%)^([6]) and more recently, fororganic field-effect transistors (hole mobilities up to 0.6 cm²V⁻¹s⁻¹).^([7])

Despite the many synthetic procedures available, the development ofgreener and cheaper synthetic procedures is desired. Greener materialsare likely to exhibit improved performance and stability, consideringthey are inherently cleaner (absence of organometallic by-products). Onepromising approach is merging the advantages of plastic solar cells withnew ecofriendly synthetic procedures. However, little is known about theproduction of green energy from green materials.

SUMMARY

The present disclosure broadly relates to the synthesis of polymers viadirect arylation or heteroarylation.

The present disclosure, in one embodiment, includes a method forpreparing a polymer comprising:

-   -   (a) treating one or more monomers, one or more catalysts and one        or more ligands under conditions for the direct arylation or        heteroarylation of the at least one monomer to provide the        polymer; and    -   (b) isolating the polymer.

In an embodiment, the polymer is a high molecular weight polymer.

In another embodiment the present disclosure includes a method forpreparing a polymer comprising:

(a) treating

-   -   (i) a monomer of Formula (I) and a monomer of Formula (II):

H*-A¹-H*  (I) and

X¹-A²-X²  (II);

-   -   (ii) one or more monomers of Formula (III):

H*-A³-X³  (III), or

-   -   (iii) a monomer of Formula (III) and a monomer of Formula (IV):

H*-A³-X³  (III) and

H*-A⁴-X⁴  (IV)

in the presence of one or more catalysts and one or more ligands underconditions for the direct arylation or heteroarylation of the monomer ofFormula (I) and monomer of Formula (II) to provide a polymer comprisingrepeating units of Formula (V):

-[A¹-A²]-  (V);

for the direct arylation or heteroarylation of the monomer of Formula(III) to provide a polymer comprising repeating units of Formula (VI):

-[A³]-  (VI); or

for the direct arylation or heteroarylation of the monomer of Formula(III) and monomer of Formula (IV) to provide a random polymer comprisingrepeating units of Formula (VII):

-[A³-A⁴]-  (VII),

whereinH* is a hydrogen that is activated for direct arylation or heteroarytionreactions;X¹, X², X³ and X⁴ are independently selected from leaving groups fordirect arylation or heteroarylation reactions; andA¹, A², A³ and A⁴ are independently selected from aryl and heteroaryl,and

(b) isolating the polymer.

In an embodiment, the present disclosure relates to a method for thesynthesis of high molecular weight conjugated polymers by directheteroarylation polycondensation reactions. In a further embodiment, thepresent disclosure relates to a method for the synthesis of highmolecular weight conjugated polymers by direct arylation reactions. Inan aspect, these direct arylation and heteroarylation polycondensationreactions provide high yields of the desired polymer product. In afurther aspect, these direct arylation and heteroarylationpolycondensation reactions provide a green alternative over the commonlyused coupling procedures often relying on organometallic reagents andintermediates.

In an embodiment, the present disclosure relates to a method forpreparing heteroaryl polymers comprising reacting one or more activatedheteroaryl monomers in the presence of one or more catalysts and one ormore ligands under conditions for the direct heteroarylation of the oneor more monomers to provide the heteroaryl polymer.

In an embodiment, the present disclosure relates to a method forpreparing heteroaryl polymers comprising reacting one or more activatedheteroaryl monomers in the presence of one or more catalysts and one ormore ligands under conditions for the direct heteroarylation orarylation of the one or more monomers to provide the heteroaryl polymer.

Interestingly, the presence of the imide group inthieno[3,4-c]pyrrole-4,6-dione (TPD) unit may act as an orienting andactivating group^([8]) for the hydrogen atoms at the 2,2′-positions(FIG. 1) and on this basis, this monomer represents a good candidate fordirect arylation or heteroarylation polycondensation reactions insteadof standard Stille cross-coupling reactions. Accordingly, an aspectincludes a method for the synthesis of TPD-based polymers via directheteroarylation. Another aspect includes a method for the synthesis ofTPD-based polymers via direct arylation. Yet another aspect includes acatalytic process for the synthesis of TPD-based polymers using directheteroarylation polycondensation reactions. Yet another aspect includesa catalytic process for the synthesis of TPD-based polymers using directarylation polycondensation reactions.

Yet a further aspect includes a method for the synthesis of2-alkylthieno[3,4-d]dithiazole-(TTZ) based polymers via directheteroarylation. Another aspect includes a method for the synthesis ofTTZ-based polymers via direct arylation. Yet another aspect includes acatalytic process for the synthesis of TTZ-based polymers using directheteroarylation polycondensation reactions. Yet another aspect includesa catalytic process for the synthesis of TTZ-based polymers using directarylation polycondensation reactions.

Yet a further aspect includes a method for the synthesis of(3,6-bis(thiophene-2-yl)-2,5-bis(2-octyldodecyl)pyrrolo[3,4-c]pyrrole-1,4(2H,5H)-dione)-(DPP)based polymers via direct heteroarylation. Another aspect includes amethod for the synthesis of DPP-based polymers via direct arylation. Yetanother aspect includes a catalytic process for the synthesis ofDPP-based polymers using direct heteroarylation polycondensationreactions. Yet another aspect includes a catalytic process for thesynthesis of DPP-based polymers using direct arylation polycondensationreactions.

Yet a further aspect includes a method for the synthesis ofisoindigo-based polymers via direct heteroarylation. Another aspectincludes a method for the synthesis of isoindigo-based polymers viadirect arylation. Yet another aspect includes a catalytic process forthe synthesis of isoindigo-based polymers using direct heteroarylationpolycondensation reactions. Yet another aspect includes a catalyticprocess for the synthesis of isoindigo-based polymers using directarylation polycondensation reactions.

Using the method of the present disclosure, certain novel polymers areprepared. Therefore, the present disclosure also includes novel polymersprepared using the methods of the disclosure.

In an embodiment of the disclosure, the present disclosure includes apolymer comprising repeating units of the Formulae (V), (VI) or (VII):

-[A¹-A²]-  (V);

-[A³]-  (VI); or

-[A³-A⁴]-  (VII),

whereinA¹, A², A³ and A⁴ are independently selected from aryl and heteroaryl,and the polymers were prepared using direct arylation or heteroarylationconditions.

In an embodiment, the present disclosure relates to the use of highmolecular weight TPD-based polymers, TTZ-based polymers, DPP-basedpolymers and isoindigo-based polymers in various electronic devices. Inan aspect, non-limiting examples of electronic devices include organicelectronic devices including photovoltaic devices, OLEDs, OPVs,transistors, OFETs, batteries, and printed electronics generally, aswell as sensors.

Other features and advantages of the present disclosure will becomeapparent from the following detailed description. It should beunderstood, however, that the detailed description and the specificexamples while indicating preferred embodiments of the disclosure aregiven by way of illustration only, since various changes andmodifications within the spirit and scope of the disclosure will becomeapparent to those skilled in the art from this detailed description.

BRIEF DESCRIPTION OF THE DRAWINGS/FIGURES

An embodiment of the disclosure will now be discussed in relation to thedrawings in which:

FIG. 1 is an illustration of the activated hydrogen atoms at the2,2′-positions of the TPD unit.

FIG. 2 is a general schematic illustration of the synthesis of copolymerP1 by both Stille and direct heteroarylation polymerization reactions.

FIG. 3a and FIG. 3b are an illustration of the UV/Vis absorption spectraof P1 and Pr: FIG. 3a ) in a chloroform solution; and FIG. 3b ) in thesolid state, in accordance with an embodiment of the present disclosure.

FIG. 4 is an illustration of the ¹H NMR spectra of P1 (top) and P1*(lower) in CDCl₃ in accordance with an embodiment of the presentdisclosure.

FIG. 5 is an illustration of the DSC thermograms for P1 and P1* inaccordance with an embodiment of the present disclosure.

FIG. 6a and FIG. 6b are an illustration of the X-ray diffractionpatterns for P1 (FIG. 6A) and P1* (FIG. 6B) in accordance with anembodiment of the present disclosure.

FIG. 7 is an illustration of the UV-vis absorption spectrum of P2 in thesolid state in accordance with an embodiment of the present disclosure.

FIG. 8 is an illustration of the UV-vis absorption spectrum of P3 in thesolid state in accordance with an embodiment of the present disclosure.

FIG. 9 is an illustration of the UV-vis absorption spectrum of P4 in thesolid state in accordance with an embodiment of the present disclosure.

FIG. 10a and FIG. 10b are an illustration of the UV-vis absorptionspectra of PCTPD synthesized by Suzuki and direct arylation reaction, inCHCl₃ solution (FIG. 10a ) and in the solid state (FIG. 10b ), inaccordance with an embodiment of the present disclosure.

FIG. 11 is an illustration of the TGA curve for PCTPD synthesized bySuzuki and by direct arylation reaction (heating rate of 20 K/min.), inaccordance with an embodiment of the present disclosure.

FIG. 12a and FIG. 12b are an illustration of the UV-vis absorptionspectrum of P5 synthesized by both Stille cross-coupling and directarylation polymerization reaction (FIG. 12a ), and a cyclic voltammogramillustrating the reduction potential of P5 (FIG. 12b ), in accordancewith an embodiment of the present disclosure.

FIG. 13A through FIG. 131 are an illustration of the UV-vis absorptionspectra for polymers P9-P17 synthesized by direct arylation reaction inboth solution and in the solid state, in accordance with an embodimentof the present disclosure.

FIG. 14 is an illustration of the UV-vis absorption spectrum of P21synthesized by direct arylation reaction, in accordance with anembodiment of the present disclosure.

FIG. 15 is an illustration of a cyclic voltammogram illustrating thereduction potential of P21, in accordance with an embodiment of thepresent disclosure.

FIG. 16 is an illustration of the UV-vis absorption spectra in CHCl₃solution for P22-29 synthesized by direct arylation reaction, inaccordance with an embodiment of the present disclosure.

FIG. 17 is an illustration of the solid state UV-vis absorption spectrafor P22-29 synthesized by direct arylation reaction, in accordance withan embodiment of the present disclosure.

FIG. 18a through FIG. 18c are an illustration of the UV-vis absorptionspectra of P37-39 in thin films and in a chloroform solution, inaccordance with an embodiment of the present disclosure.

FIG. 19a through FIG. 19C are an illustration of cyclic voltammogramsillustrating the reduction potential of isoindigo copolymers P37-39, inaccordance with an embodiment of the present disclosure.

DETAILED DESCRIPTION I. Glossary

In order to provide a clear and consistent understanding of the termsused in the present specification, a number of definitions are providedbelow. Moreover, unless defined otherwise, all technical and scientificterms as used herein have the same meaning as commonly understood by oneof ordinary skill in the art to which this specification pertains.

The word “a” or “an” when used in conjunction with the term “comprising”in the claims and/or the specification may mean “one”, but it is alsoconsistent with the meaning of “one or more”, “at least one”, and “oneor more than one” unless the content clearly dictates otherwise.Similarly, the word “another” may mean at least a second or more unlessthe content clearly dictates otherwise.

As used in this specification and claim(s), the words “comprising” (andany form of comprising, such as “comprise” and “comprises”), “having”(and any form of having, such as “have” and “has”), “including” (and anyform of including, such as “include” and “includes”) or “containing”(and any form of containing, such as “contain” and “contains”), areinclusive or open-ended and do not exclude additional, unrecitedelements or process steps.

As used in this specification and claim(s), the word “consisting” andits derivatives, are intended to be close ended terms that specify thepresence of stated features, elements, components, groups, integers,and/or steps, and also exclude the presence of other unstated features,elements, components, groups, integers and/or steps.

The term “consisting essentially of”, as used herein, is intended tospecify the presence of the stated features, elements, components,groups, integers, and/or steps as well as those that do not materiallyaffect the basic and novel characteristic(s) of features, elements,components, groups, integers, and/or steps.

The terms “about”, “substantially” and “approximately” as used hereinmean a reasonable amount of deviation of the modified term such that theend result is not significantly changed. These terms of degree should beconstrued as including a deviation of at least ±1% of the modified termif this deviation would not negate the meaning of the word it modifies.

The present description refers to a number of chemical terms andabbreviations used by those skilled in the art. Nevertheless,definitions of selected terms are provided for clarity and consistency.

Abbreviations: NMR: Nuclear Magnetic Resonance; MS: Mass Spectrometry;m.p.: melting point; HRMS: High Resolution Mass Spectrometry; SEC:Size-Exclusion Chromatography; M_(n): Number Average Molecular Weight;PDI: PolyDispersity Index; DP: Degree of Polymerization; DSC:Differential Scanning Calorimtry, TGA: Thermogravimetric Analysis; XRD:SEC: Size Exclusion Chromatography; X-Ray Diffraction (powderdiffraction); PDI: PolyDispersity Index; EtOAc: Ethyl Acetate; CH₂Cl₂:Dichloromethane, CDCl₃: Chloroform-d; DMAP:4-(N,N-dimethylamino)pyridine; TFA: Trifluoroacetic acid; TCDI:1,1-thiocarbonyldiimidazole, AcOH: Acetic acid; TLC: Thin LayerChromatography; FAB: Fast Atom Bombardment; FCC: Flash ColumnChromatography.

As used herein, the term “alkyl” embraces straight-chain or branchedchain saturated hydrocarbons. Substituted alkyl groups can besubstituted in any suitable position. Examples of alkyl groupscontaining from 1 to 18 carbon atoms are methyl, ethyl, propyl, butyl,pentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl,tetradecyl, hexadecyl and octadecyl, the n-isomers of all theseresidues, isopropyl, isobutyl, isopentyl, neopentyl, isohexyl, isodecyl,3-methylpentyl, 2,3,4-trimethylhexyl, sec-butyl, tert-butyl, ortert-pentyl. A specific selection of alkyl groups consists of methyl,ethyl, n-propyl, isopropyl, n-butyl, isobutyl, sec-butyl and tert-butyl.

As used herein, the term “lower alkyl” embraces straight-chain orbranched-chain saturated hydrocarbons containing 1, 2, 3, 4, 5 or 6carbon atoms. Substituted alkyl groups can be substituted in anysuitable position. Examples of lower alkyl groups are methyl, ethyl,propyl, isopropyl, butyl, isobutyl, tert-butyl, pentyl, isopentyl,neopentyl, and hexyl.

As used herein, the term “alkylene” embraces a linear saturated divalenthydrocarbon group of one to six carbon atoms or a branched-chainsaturated divalent hydrocarbon group of three to six carbon atoms.Examples of alkylene groups are methylene, ethylene,2,2-dimethylethylene, propylene, 2-methylpropylene, butylene, andpentylene.

As used herein the term “alkenyl” embraces straight-chain orbranched-chain unsaturated hydrocarbons that contain one or more, forexample one, two or three double bonds which can be in any suitableposition. Of course, an unsaturated alkyl group has to contain at leasttwo carbon atoms. Examples of alkenyl groups are vinyl, 1-propenyl,allyl, butenyl or 3-methyl-2-butenyl.

As used herein the term “alkynyl” embraces straight-chain orbranched-chain unsaturated alkyl groups that contain one or more, forexample one, two or three, triple bonds which can be in any suitableposition. Of course, an unsaturated alkyl group has to contain at leasttwo carbon atoms. Examples of alkynyl groups are ethynyl, 1-propynyl orpropargyl.

As used herein the term “cycloalkyl” embraces monocyclic or polycyclichydrocarbons, for example monocyclic, bicyclic, tricyclic orquadracyclic, i.e., they can for example be monocycloalkyl groups,bicycloalkyl groups, tricycloalkyl groups, or quadracycloalkyl groups,provided they have a suitable number of carbon atoms, for example from 3to 30 carbon atoms, and the parent hydrocarbon systems are stable.Bicyclic, tricyclic or quadracyclic alkyl groups are fused, bridgedand/or simply linked via a single bond. Cycloalkyl groups can besaturated or contain one or more double bonds within the ring system. Inparticular they can be saturated or contain one double bond within thering system. In unsaturated cycloalkyl groups the double bonds can bepresent in any suitable position. Monocycloalkyl residues are, forexample, cyclopropyl, cyclobutyl, cyclopentyl, cyclopentenyl,cyclohexyl, cyclohexenyl, cycloheptyl, cycloheptenyl, cyclooctyl,cyclononyl, cyclodecyl, cycloundecyl, cyclododecyl or cyclotetradecyl,which can also be substituted, for example by C₁-C₄ alkyl. Examples ofsubstituted cycloalkyl groups are 4-methylcyclohexyl and2,3-dimethylcyclopentyl. Examples of parent structures of bicyclic ringsystems are norbornane, bicyclo[2.2.1]heptane, bicyclo[2.2.2]octane andbicyclo[3.2.1]octane.

As used herein, the term “aryl” embraces an aromatic group which is asingle ring or multiple rings fused, bridged or linked together viasingle bond. When formed of multiple rings, at least one of theconstituent rings is aromatic. In an embodiment, aryl substituentsinclude phenyl, indanyl, biphenyl and naphthyl.

The term “halo” means the halogens fluorine, chlorine, bromine oriodine.

The term “heterocyclo” as used herein embraces saturated and partiallyunsaturated heteroatom-containing cyclic groups, where the heteroatomsare selected from nitrogen, sulfur and oxygen. The heterocyclo groupsare either monocyclic, bicyclic, tricyclic or quadracyclic, providedthey have a suitable number of atoms, for example from 3 to 30 atoms,and are stable. A bicyclic, tricyclic or quadraheterocyclo group can befused, bridged and/or simply linked via a single bond. Examples ofsaturated heterocyclo groups include saturated 3 to 6-memberedheteromonocyclic groups containing 1 to 4 nitrogen atoms (e.g.pyrrolidinyl, imidazolidinyl, piperidino, piperazinyl, etc.); saturated3 to 6-membered heteromonocyclic groups containing 1 to 2 oxygen atomsand 1 to 3 nitrogen atoms (e.g. morpholinyl, etc.); saturated 3 to6-membered heteromonocyclic groups containing 1 to 2 sulfur atoms and 1to 3 nitrogen atoms (e.g., thiazolidinyl, etc.). Examples of partiallyunsaturated heterocyclo groups include dihydrothiophene, dihydropyran,dihydrofuran and dihydrothiazole.

The term “heteroaryl” as used herein embraces fully unsaturated oraromatic heterocyclo groups. The heteroaryl groups are eithermonocyclic, bicyclic, tricyclic or quadracyclic, provided they have asuitable number of atoms, for example from 3 to 30 atoms, and arestable. A bicyclic, tricyclic or quadraheteroaryl groups are fused,bridged and/or simply linked via a single bond. Examples of heteroarylgroups, include unsaturated 3 to 6 membered heteromonocyclic groupscontaining 1 to 4 nitrogen atoms, for example, pyrrolyl, pyrrolinyl,imidazolyl, pyrazolyl, pyridyl, pyrimidyl, pyrazinyl, pyridazinyl,triazolyl (e.g., 4H-1,2,4-triazolyl, 1H-1,2,3-triazolyl,2H-1,2,3-triazolyl, etc.) tetrazolyl (e.g. 1H-tetrazolyl, 2H-tetrazolyl,etc.), etc.; unsaturated condensed heterocyclo groups containing 1 to 5nitrogen, oxygen and/or sulfur atoms, for example, indolyl, isoindolyl,indolizinyl, benzimidazolyl, quinolyl, isoquinolyl, indazolyl,benzotriazolyl, tetrazolopyridazinyl (e.g., tetrazolo[1,5-b]pyridazinyl,etc.), benzofuran, benzothienyl, benzopyran, etc.; unsaturated 3 to6-membered heteromonocyclic groups containing an oxygen atom, forexample, pyranyl, furyl, etc.; unsaturated 3 to 6-memberedheteromonocyclic groups containing a sulfur atom, for example, thienyl,etc.; unsaturated 3- to 6-membered heteromonocyclic groups containing 1to 2 oxygen atoms and 1 to 3 nitrogen atoms, for example, oxazolyl,isoxazolyl, oxadiazolyl (e.g., 1,2,4-oxadiazolyl, 1,3,4-oxadiazolyl,1,2,5-oxadiazolyl, etc.) etc.; unsaturated condensed heterocyclo groupscontaining 1 to 2 oxygen atoms and 1 to 3 nitrogen atoms (e.g.benzoxazolyl, benzoxadiazolyl, etc.); unsaturated 3 to 6-memberedheteromonocyclic groups containing 1 to 2 sulfur atoms and 1 to 3nitrogen atoms, for example, thiazolyl, thiadiazolyl (e.g.,1,2,4-thiadiazolyl, 1,3,4-thiadiazolyl, 1,2,5-thiadiazolyl, etc.) etc.;unsaturated condensed heterocyclo groups containing 1 to 2 sulfur atomsand 1 to 3 nitrogen atoms (e.g., benzothiazolyl, benzothiadiazolyl,etc.) and the like.

As used herein, the term “high molecular weight” will depend on the typeof polymer, but will generally denote molecular weights in excess ofabout 10 kDa.

As used herein, the term “direct heteroarylation” or “direct arylation”means that none of the monomers used in the heteroarylation or arylationprocess comprises a sacrificial organometallic functionality at theposition of the coupling. Heteroarylation occurs when the monomerscomprise at least one heteroaryl. Arylation occurs when all of themonomers are aryl. Organometallic refers to compounds which have anorganic group bonded to a metal or metalloid through a carbon-metalbond. A non-limiting example of an organometallic is an organotincompound such as frequently encountered in Stille Coupling reactions.

As used herein, “under conditions for the direct arylation orheteroarylation” refers to the reaction conditions used to effect thecoupling of aryl and/or heteroaryl monomers in the presence of one ormore ligands and one or more catalysts as used herein. In an embodiment,these conditions comprise, consist of or consist essentially of thecombining of the one or more monomers, ligands and catalysts under aninert atmosphere and optionally with an inert solvent, followed byheating. In an embodiment, the one or more monomers, ligands andcatalysts and optional solvent are heated to a temperature of about 50°C. to about 200° C., or about 100° C. to about 150° C. In an embodimentan inert organic solvent is used to substantially dissolve the one ormore monomers, ligands and catalysts.

The term “inert solvent” as used herein refers to any solvent or mixtureof solvents in which the reagents in a chemical reaction aresubstantially soluble, at least to the extent to allow the chemicalreaction, and which does not interfere with or inhibit the chemicalreaction. The selection of a suitable inert solvent is well within theskill of a person in the art.

The expression “hydrogen that is activated for direct arylation orheteroarytion reactions” as used here in refers to hydrogen atoms on anaryl or heteroaryl group that, due to the specific structure orsubstitution patterns of the aryl or heteroaryl group, are reactiveunder direct arylation or heteroarylation conditions. By “reactive underdirect arylation or heteroarylation conditions” it is meant toparticipate in the reaction with the catalyst(s) and ligand(s) to resultin bond formation between the carbon to which the activated hydrogen isattached and a carbon to which an “X” group is attached on a second arylor heteroaryl group. A hydrogen is activated, for example, by attachingan electron withdrawing group at a position alpha to the carbon atomcontaining the activated hydrogen. Non-limiting examples of electronwithdrawing groups are carbonyl-containing functional groups (C(O)—R),cyano and nitro. wherein R is alkyl, cycloalkyl or O-alkyl.Alternatively, a heteroatom, such as O or S, may be located alpha to thecarbon atom containing the activated hydrogen. The term “substituted” asused herein, means that a hydrogen atom of the designated moiety isreplaced with a specified substituent, provided that the substitutionresults in a stable or chemically feasible compound. Non-limitingexamples of substituents include halogen (F, Cl, Br, or I) for exampleBr, ON, C(O)—R and alkyl groups, wherein R is alkyl, cycloalkyl orO-alkyl.

The term “suitable” as used herein means that the selection of theparticular compound or conditions would depend on the specific syntheticmanipulation to be performed, and the identity of the molecule(s) to betransformed, but the selection would be well within the skill of aperson trained in the art. All process/method steps described herein areto be conducted under conditions sufficient to provide the productshown. A person skilled in the art would understand that all reactionconditions, including, for example, reaction solvent, reaction time,reaction temperature, reaction pressure, reactant ratio and whether ornot the reaction should be performed under an anhydrous or inertatmosphere, can be varied to optimize the yield of the desired productand it is within their skill to do so.

The expression “proceed to a sufficient extent” as used herein withreference to the reactions or process steps disclosed herein means thatthe reactions or process steps proceed to an extent that conversion ofthe starting material or substrate to product is maximized. Conversionmay be maximized when greater than about 5, 10, 15, 20, 25, 30, 35, 40,45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95 or 99% of the startingmaterial or substrate is converted to product.

Further, the definitions and embodiments described in particularsections are intended to be applicable to other embodiments hereindescribed for which they are suitable as would be understood by a personskilled in the art. For example, in the following passages, differentaspects of the invention are defined in more detail. Each aspect sodefined may be combined with any other aspect or aspects unless clearlyindicated to the contrary. In particular, any feature indicated as beingpreferred or advantageous may be combined with any other feature orfeatures indicated as being preferred or advantageous.

Methods for Preparing Polymers

In one of its embodiments, the present disclosure includes a method forpreparing a polymer comprising:

-   -   (a) treating one or more monomers, one or more catalysts and one        or more ligands under conditions for the direct arylation or        heteroarylation of the at least one monomer to provide the        polymer; and    -   (b) isolating the polymer.

In another embodiment the present disclosure includes a method forpreparing a polymer comprising:

(a) treating

-   -   (i) a monomer of Formula (I) and a monomer of Formula (II):

H*-A¹-H*  (I) and

X¹-A²-X²  (II);

-   -   (ii) one or more monomers of Formula (III):

H*-A³-X³  (III), or

-   -   (iii) a monomer of Formula (III) and a monomer of Formula (IV):

H*-A³-X³  (III) and

H*-A⁴-X⁴  (IV),

in the presence of one or more catalysts and one or more ligands underconditions for the direct arylation or heteroarylation of the monomer ofFormula (I) and monomer of Formula (II) to provide a polymer comprisingrepeating units of Formula (V):

-[A¹-A²]-  (V);

for the direct arylation or heteroarylation of the monomer of Formula(III) to provide a polymer comprising repeating units of Formula (VI):

-[A³]-  (VI); or

for the direct arylation or heteroarylation of the monomer of Formula(III) and monomer of Formula (IV) to provide a random polymer comprisingrepeating units of Formula (VII):

-[A³-A⁴]-  (VII),

whereinH* is a hydrogen that is activated for direct arylation orheteroarylation reactions;X¹, X², X³ and X⁴ are independently selected from leaving groups fordirect arylation or heteroarylation reactions; andA¹, A², A³ and A⁴ are independently selected from aryl and heteroaryl;and

(b) isolating the polymer.

In an embodiment of the disclosure, the method further comprises, priorto isolating the polymer, adding an end capping reagent to the polymer.End capping reagents are monomers, such as monomers of Formula I, thatdo no comprise a leaving group for direct arylation or heteroarylationreactions.

In an embodiment, the leaving groups for direct arylation andheteroarylation are selected from bromine and iodine. In a furtherembodiment, the leaving group is bromine.

In an embodiment of the disclosure, aryl is selected from phenyl,biphenyl, naphthyl and indanyl. In another embodiment, aryl is phenyl.

It is an embodiment of the present disclosure that A¹, A², A³ and A⁴ areindependently selected heteroaryl. In a further embodiment, heteroarylcomprises at least one thienyl group. In a further embodiment, the atleast one thienyl group is fused to a 5-membered or 6-memberedheterocyclo group. In a further embodiment, the heteroaryl comprises alinear chain of 2, 3 or 4 thienyl groups. In another embodiment,heteroaryl comprises an oxindole group, an indigo group or isoindigogroup.

In yet another embodiment, the heteroaryl group is selected from:

Wherein R¹, R^(1′), R², R³, R⁴, R⁵, R⁶, R⁷, R⁸, R⁹, R¹⁰, R¹¹, R¹², R¹³,R¹⁴, R¹⁵, R¹⁶, R¹⁷, R¹⁸, R¹⁹, R²⁰, R²¹, R²², R²³, R²⁴, R²⁵, R²⁶, R²⁷,R²⁸, R²⁹ and R³⁰ are independently selected from H, CN and C₁₋₃₀alkyl.In an embodiment, R¹, R^(1′), R², R³, R⁴, R⁵, R⁶, R⁷, R⁸, R⁹, R¹⁰, R¹¹,R¹², R¹³, R¹⁴, R¹⁵, R¹⁶, R¹⁷, R¹⁸, R¹⁹, R²⁰, R²¹, R²², R²³, R²⁴, R²⁵,R²⁶, R²⁷, R²⁸, R²⁹ and R³⁰ are independently selected from C₁₋₃₀alkyl.

In an embodiment of the disclosure, the one or more ligands are trialkylor triaryl phosphines, in which the alkyl and aryl groups aresubstituted or unsubstituted, or the corresponding phosphonium salts, orcomplexes thereof with metals such as palladium. Examples ofsubstituents on the alkyl and aryl groups are C₁₋₆alkyl, OC₁₋₆alkyl andN(C₁₋₆alkyl)₂. Examples of phosphonium salts are HBF₄ salts. In afurther embodiment of the disclosure, the one or more ligands areselected from: P(t-Bu)₃HBF₄, P(Cy)₃HBF₄, P(t-Bu)₂MeHBF₄, P(o-tol)₃,

In an embodiment of the disclosure, the catalyst is a palladium (II)catalyst. In a further embodiment, the palladium catalyst isPd(OAc)(o-Tol) or Pd(OAc)₂.

The methods of preparing polymers of the present disclosure areperformed using direct arylation (if all monomers comprise only arylgroups) or heteroarylation (in at least one of the monomers comprise andheteroaryl group) conditions. In the polymerization reactions, bonds areformed between atoms in the aryl or heteroaryl groups. As noted above,arylation and heteroarylation conditions comprise, consist of, orconsist essentially of reacting the one or more monomers, one or moreligands and one or more catalysts under an inert atmosphere, typicallyin an inert solvent (although a person skilled in the art wouldappreciate that the reaction could be performed without solvent, forexample, if one of the reactants is a liquid in which the otherreactants are soluble), and with heating. Inert atmosphere includes, forexample, under nitrogen or argon. Heating temperatures will varydepending on the reactants, however, will generally be about 50° C. toabout 200° C., or about 100° C. to about 150° C. Reaction times willalso vary depending on the reactants, but can be determined usingmethods known in the art, for example, by following the reactionprogress by thin layer chromatography (TLC) or nuclear magneticresonance (NMR) spectroscopy, and monitoring the disappearance ofstarting materials and/or formation of product. Reactions will becomplete when a sufficient amount of the product is formed. Reactionsolvents, temperatures and times are parameters that are readilyselected by a person of skill in the art.

The amount and ratio of monomers used in the methods of the applicationwill depend on the desired polymeric structure. If more than one monomeris present, each will be used in an amount that corresponds to thedesired ratio of monomers in the final polymer.

In an embodiment the one or more catalysts are used in an amount ofabout 0.1 mol % to about 5 mol % based on the amount of monomers used.In a further embodiment, the one or more catalysts are used in an amountof about 1 mol % to about 3 mol %, or about 2 mol %, based on the amountof monomers used.

In an embodiment the one or more ligands are used in an amount of about5 mol % to about 20 mol % based on the amount of monomers used. In afurther embodiment, the one or more catalysts are used in an amount ofabout 7 mol % to about 10 mol %, or about 8 mol %, based on the amountof monomers used.

In a further embodiment, the method of the disclosure also includes theaddition of one or more mild bases along with the one or more monomers,one or more catalysts and one or more ligands under conditions for thedirect arylation or heteroarylation of the at least one monomer toprovide the polymer. In an embodiment, the one or more mild bases are aninorganic mild base, such as, for example, Cs₂CO₃.

In an embodiment of the present disclosure, the methods further compriseadding an end-capping reagent after step (a) prior to isolating thepolymer. To add the end-capping reagent, it is an embodiment that one ormore monomers, ligands and catalysts that have been treated under directarylation or heteroarylation conditions are cooled and the end-cappingreagent added and the resulting mixture re-heated for a time sufficientfor the end-capping procedure to be completed, for example about 30minutes to about 2 hours. In an embodiment, the end-capping reagent is amonomer used in the polymerization reaction but that does not comprisinga leaving group.

The polymers of the present disclosure may be isolated using methodsknown in the art. In an embodiment, the polymers are isolated by coolingthe reaction mixture following by precipitation, extraction, and/orchromatography.

Representative, non-limiting examples of methods of preparing specificpolymers of the disclosure are described below.

Synthesis of Copolymer P1

As shown in FIG. 2, copolymer P1 was synthesized by both Stille anddirect heteroarylation polymerization reactions. This copolymer is ananalog of other TPD-based copolymers recently reported in highlyefficient plastic solar cells^([6c,9]) and field-effecttransistors.^([7]) Stille polymerization was carried out following knownliterature procedures (yield of 71% for the soluble fraction inchloroform). In agreement with previous polystyrene-calibrated SEC datareported for similar copolymers,^([6c,7,9]) Stille-polymerized P1* showsa M_(n) of only 9 kDa. This relatively low average molecular weight islikely due to losses of some functional groups during the Stillepolymerization.

In order to prepare P1 by means of direct heteroarylationpolycondensation, several reaction conditions were tested (Table 1). Theoptimal reaction conditions were obtained using ligand (L) 1 andcatalyst (Cat) 1. For the synthesis of P1, palladium acetate (2) is notas efficient as catalyst (1). It is surmised that this is probably dueto the higher thermal stability of the Hermann catalyst.^([5a]) Thetemperature, time, solvent, and concentration were keptconstant.^([3a-h, 5a-c]) A high M_(n) of 56 kDa (PDI of 2.6) and a yieldof 96% (soluble fraction in chloroform) was obtained for reaction R1.Additional examples of polymerizations of TPD-based monomers using thesame catalytic system are disclosed herein below in the experimentalsection.

Various spectroscopic methods were utilized in order to furthercharacterize the polymers. For instance, the UV-vis absorption spectraof P1 and P1* exhibit similar features (FIG. 3a ) with an absorptionmaximum at 470 nm in chloroform solution. This absorption maximum is ingood agreement with previous data reported for similar alternatingcopolymers.^([7,9]) On the other hand, the solid-state UV-vis absorptionspectra are slightly different (FIG. 3b ). The absorption maximum of P1(598 nm) is red shifted by approximately 26 nm compared to P1* (572 nm).Apart the absorption maxima, these UV-vis absorption spectra are quitesimilar; showing a vibronic fine structure and a bandgap of about 1.75eV. This small difference for the UV-vis spectra is likely a directresult of the different molecular weights and/or a slightly differentmorphology in the solid state.

The ¹H NMR spectra confirmed that both P1 and P1* correspond to analternating copolymer (FIG. 4). These ¹H NMR spectra are substantiallysimilar to those previously reported by Marks et al.^([7]) for analogouspolymers, the only difference being the alkyl side-chains. As previouslyreported, different small peaks can be observed for P1* around 6.8-7.1,3.5, and 2.7 ppm, which are likely due to the end-groups. Notsurprisingly, such extra peaks are barely observed for the highmolecular weight P1 copolymer. Moreover, for both P1 and P1*, a smallbroad peak (with a relative integration of about 2%) can be observednear 2.55 ppm, which may be tentatively related to some end groupsand/or the presence of some bithiophene-bithiophene couplings (a sidereaction), leading to so-called head-to-head couplings.^([10]) Thisextra and broad peak can also be observed in some ¹H NMR spectrareported by Marks et al. for similar copolymers.

To further validate the structural regularity of these alternatingcopolymers, thermal and X-ray analyses were performed. The DSCthermograms of both P1 and P1* present some well-defined crystallisationand melting peaks (FIG. 5). The enthalpies of crystallisation (

H_(c)) and melting (

H_(m)) are slightly higher for P1 (

H_(c)=16.4 J/g and L H_(m)=15.4 J/g) than for P1* (

H_(c)=14.6 J/g and

H_(m)=14.3 J/g) which indicates a more important degree of crystallinityfor P1. The higher melting point for P1 also indicates a betterstability of the crystal, which is probably related to the highermolecular weight. The XRD diffraction patterns (FIG. 6) show similarfeatures for both polymers, indicative that P1 and P1* are similarlyorganized in the solid state. Consequently, the red-shifted solid-stateoptical spectrum of P1 (FIG. 3b ) should be mainly related to a highermolecular weight.

Synthesis of Copolymers P5, P6-P8, P9-P20, P21, P22-29, P30-33, P34-36and P37-39

As shown in Scheme 1 hereinbelow, copolymer P5 was synthesized by bothStille cross-coupling and direct heteroarylation polymerizationreactions. Polymers P6-P8 were prepared by direct heteroarylationpolymerization reactions (c.f. Scheme 20). Polymers P9-P20 were preparedby direct heteroarylation polymerization reactions (c.f. Experimentalsection). The synthesis of polymer P21 by direct heteroarylation isillustrated in Scheme 2. The synthesis polymers P22-29 by directheteroarylation is illustrated in Scheme 3. The synthesis polymersP30-33 by direct heteroarylation is illustrated in Scheme 21. Thesynthesis polymers P34-36 by direct heteroarylation is illustrated inScheme 22. The synthesis polymers P37-39 by direct heteroarylation isillustrated in Schemes 23-25.

Various spectroscopic methods were utilized in order to furthercharacterize P5 (FIG. 12). The number average molecular weight (M_(n)),weight average molecular weight (M_(w)) and polydispersity index (I_(p))for P5 as obtained by both Stille cross-coupling and directheteroarylation polymerization, are illustrated in Table 2. Variousoptical and electronic properties for polymers P9-P18 are illustrated inTable 3. Various physical, optical and electronic properties for polymerP21 are illustrated in Table 4. Various physical, thermal, spectroscopicand electrochemical properties for polymers P22-29 are illustrated inTables 5 and 6.

The monomers can be prepared using methods available in the art.Exemplary methods for the preparation of various intermediates andmonomers (2-18, 29-31) to be used in the direct heteroarylationpolycondensation reactions, in accordance with an embodiment of thepresent disclosure, is illustrated herein below in Schemes 4-16.

Synthesis of Intermediate 3

Synthesis of Monomer 4

Synthesis of Monomer 6

Synthesis of Monomer 7

Synthesis of Monomer 8

Synthesis of Monomer 9

Synthesis of Monomer 10

Synthesis of Monomer 12

Synthesis of Monomer 13

Synthesis of Monomers 14-16

Synthesis of Monomers 17 and 18

Synthesis of Monomer 29

Synthesis of Monomers 30 and 31

Additional monomers (19-28), in accordance with an embodiment of thepresent disclosure, are illustrated hereinbelow in Schemes 17, 18 and19.

The synthesis of additional copolymers P6-P8 by direct heteroarylationis illustrated hereinbelow in Scheme 20.

The synthesis of additional copolymers P30-P33 by direct heteroarylationis illustrated hereinbelow in Scheme 21.

The synthesis of additional copolymers P34-P39 by direct heteroarylationis illustrated hereinbelow in Schemes 22-25.

Various physical, thermal, spectroscopic and electrochemical propertiesfor P37-39 are illustrated in Tables 7.

Polymers of the Disclosure

Using the method of the present disclosure, certain novel polymers areprepared. Therefore, the present disclosure also includes novel polymersprepared using the methods of the disclosure.

In an embodiment of the disclosure, the present disclosure includes apolymer comprising repeating units of the Formulae (V), (VI) or (VII):

-[A¹-A²]-  (V);

-[A³]-  (VI); or

-[A³-A⁴]-  (VII),

whereinA¹, A², A³ and A⁴ are independently selected from aryl and heteroaryl,and the polymers were prepared using direct arylation or heteroarylationconditions.

It is an embodiment of the present disclosure that A¹, A², A³ and A⁴ areindependently selected heteroaryl. In a further embodiment, heteroarylcomprises at least one thienyl group. In a further embodiment, the atleast one thienyl group is fused to a 5-membered or 6-memberedheterocyclo group. In a further embodiment, the heteroaryl comprises alinear chain of 2, 3 or 4 thienyl groups. In another embodiment,heteroaryl comprises an oxindole group, and indigo or isoindigo group.

In yet another embodiment, A¹, A², A³ and A⁴ are independently selectedfrom:

wherein R¹, R^(1′), R², R³, R⁴, R⁵, R⁶, R⁷, R⁸, R⁹, R¹⁰, R¹¹, R¹², R¹³,R¹⁴, R¹⁵, R¹⁶, R¹⁷, R¹⁸, R¹⁹, R²⁰, R²¹, R²², R²³, R²⁴, R²⁵, R²⁶, R²⁷,R²⁸, R²⁹ and R³⁰ are independently selected from H, CN and C₁₋₃₀alkyland

denotes the point of attachment with the adjacent “A” group. In anembodiment, R¹, R^(1′), R², R³, R⁴, R⁵, R⁶, R⁷, R⁸, R⁹, R¹⁰, R¹¹, R¹²,R¹³, R¹⁴, R¹⁵, R¹⁶, R¹⁷, R¹⁸, R¹⁹, R²⁰, R²¹, R²², R²³, R²⁴, R²⁵, R²⁶,R²⁷, R²⁸, R²⁹ and R³⁰ are independently selected from C₁₋₃₀alkyl.

In an embodiment of the disclosure, at least one of A¹, A², A³ and A⁴ isindependently selected from phenyl, biphenyl, naphthyl and indanyl, inparticular, phenyl.

In an embodiment, the polymers of the disclosure are high molecularweight polymers. For example, the polymers prepared using the methods ofthe present disclosure have a higher molecular weight than correspondingpolymers using alternative methods such as Stille coupling reactions. Ina further embodiment, the polymers of the present disclosure do notcomprise metals that are used in alternative methods, such as tin usedin the Stille coupling reactions.

In a further embodiment of the disclosure, there is included a polymerselected from the group consisting of:

wherein n is the number of repeating units in the polymer chain. In anembodiment n ranges from 10 to 100.

EXPERIMENTAL

A number of examples are provided herein below illustrating thepreparation of high molecular weight TPD-based polymers, TTZ-basedpolymers, DPP-based polymers and isoindigo-based polymers by directheteroarylation polycondensation reactions. The following non-limitingexamples are illustrative of the present disclosure.

Materials

Chemicals:

Thiophene-3,4-dicarboxylic acid was bought from Frontier Scientific andall other starting organic compounds and organometallic compounds werepurchased from Aldrich, TCI, Puyang Huicheng and used without anyfurther purification. The reaction solvents were distilled under inertatmosphere prior to use (THF from sodium/benzophenone, acetonitrile fromCaH₂), all other solvents were usually ACS grade.2,7-Bis(4′,4′,5′,5′-tetramethyl-1′,3′,2′-dioxaborolan-2′-yl)-N-9′-heptadecanylcarbazole,1-iodo-5-octyl-4H-thieno[3,4-c]pyrrole-4,6(5H)-dione,5-octyl[3,4-c]pyrrole-4,6-dione, 5-dodecyl[3,4-c]pyrrole-4,6-dione,5-(2-Octyldodecyl)thieno[3,4]pyrrole-4,6-dione, 2-Hexyldecan-1-amine(compound 3, Scheme 4), 5,5′-dibromo-4,4′-dioctyl-2,2′-bithiophene(compound 6, Scheme 6),4,4′-dioctyl-5,5′-bis(trimethylstannyl)-2,2′-bithiophene (compound 7,Scheme 7), 1,3-dibromo-5-(2-Hexyldecyl)thieno[3,4]pyrrole-4,6-dione(compound 8, Scheme 8), Tris-(o-dimethylaminophenyl)phosphine, trans-di(

-acetato)-bis[

(di-o-tolylphosphino)benzyl]dipalladium(II),2-iodothiophene-3,4-dicarboxylic acid, bromooxindole and isoindigo wereprepared according to known literature procedures. All the monomers werecarefully purified prior to use in the polymerization reactions.

Instrumentation/Characterization:

¹H and ¹³C NMR spectra were recorded using a Varian A5400 in deuteratedchloroform or acetone solution at 298° K. Number-average (M_(n)) andweight-average (M_(w)) molecular weights were determined by sizeexclusion chromatography (SEC) using a Varian Instrument PL120 withStyrene-DVB gel columns in CHCl₃ at 25° C. For the calibration curve, aseries of monodisperse polystyrene standards (Shodex) were used.Thermogravimetric analysis (TGA) measurements were carried out using aMettler Toledo TGA SDTA 851e apparatus (heating rate of 20° C./min undernitrogen flow) and the temperature of degradation (T_(d)) corresponds toa 5% weight loss. Differential scanning calorimetry (DSC) analyses wereperformed using a Mettler Toledo DSC823e instrument, calibrated withultrapure indium, at a scanning rate of 20° C./min under a nitrogenflow. Glass transition temperatures (T_(g)) were determined using ascanning rate of 20° C./min under a nitrogen flow. UV-vis-NIR absorptionspectra were recorded using a Varian Cary 500 and dropcast films onglass plates were utilized for solid-state measurements. Opticalbandgaps were determined from the onset of the absorption band. Cyclicvoltammograms (CV) were recorded on a Solartron 1287 potentiostat usingplatinum wires as the working electrode and counter-electrode at a scanrate of 50 mV/s. The reference electrode was Ag/Ag⁺ (0.1 M of AgNO₃ inacetonitrile) and the electrolyte was a solution of 0.1 M oftetrabutylammonium tetrafluoborate in dry acetonitrile. Under theseconditions, the oxidation potential of Ferrocene was 0.09 V versusAg/Ag, whereas the oxidation potential of Ferrocene was 0.41 V versusSCE. The HOMO and LUMO energy levels were determined from the oxidationand reduction onsets (where the current differs from the baseline)assuming that the SCE electrode is −4.7 eV from vacuum. Small-angleX-ray diffraction (SAXD) spectra were obtained using an X-raydiffractometer (Siemens/Bruker, Kristalloflex 760 generator, three cyclegoniometer, Hi-Star area detector with GADDS software) using a graphitemonochromatized copper radiation (Kα=1.5418 Å). The operation power was40 kV, 20 mA and the collimator was 0.8 mm in diameter. The samples wereinserted in 0.01 mm thin walled glass capillary tubes (1.0 mm diameter).

Synthesis of 5-(2-Hexyldecyl)thieno[3,4]pyrrole-4,6-dione (4)

A solution of thiophene-3,4-dicarboxylic acid (5.00 g, 29.04 mmol) inacetic anhydride (270 mL) was stirred at 75° C. over a period of 2hours. The solvent was removed and to the crude product was subsequentlyadded dioxane (250 mL), DMAP (3.56 g, 43.76 mmol) and2-hexyldecan-1-amine (3) (9.45 g, 43.46 mmol). The resulting solutionwas stirred at 55° C. over a period of 20 hours. Acetic anhydride (160mL) was then added and the reaction mixture was stirred for anadditional 4 hours at 80° C. The reaction was subsequently quenched withwater (300 mL) and was extracted with dichloromethane (4×40 mL). Thecombined organic layers were dried with MgSO₄ and evaporated to drynessto yield a dark oil. The crude product was purified by columnchromatography using dichloromethane/hexane (1:2) as the eluent toafford the title product as a white oil (7.30 g, yield: 66%). ¹H NMR(400 MHz, CDCl₃) δ 7.81 (s, 2H), 3.52 (d, 2H, J=7.5 Hz), 1.83 (m, 1H,),1.40-1.15 (m, 24H), 0.87 (m, 6H), ¹³C NMR (100 MHz, CDCl₃) δ 163.2,136.9, 125.7, 43.0, 37.1, 32.12, 32.04, 31.7, 30.2, 29.87 (two peaksoverlap), 29.78, 29.53, 26.48, 26.45, 22.90, 22.87, 14.36, 14.33 ppm.

Synthesis of 1-Iodo-5-(2-hexyldecyl)thieno[3,4]pyrrole-4,6-dione (9)

A solution of 2-iodothiophene-3,4-dicarboxylic acid (7) (10.26 g, 29.04mmol) in acetic anhydride (270 mL) was stirred at 75° C. over a periodof 2 hours. The solvent was removed and to the crude product was addeddioxane (250 mL), DMAP (3.56 g, 43.76 mmol) and 2-hexyldecan-1-amine(10.49 g, 43.46 mmol). The resulting solution was subsequently stirredat 55° C. over a period of 20 hours. Acetic anhydride (160 mL) was thenadded and the reaction mixture was stirred for an additional 4 hours at80° C. The reaction was subsequently quenched with water (300 mL) andwas extracted with dichloromethane (4×40 mL). The combined organiclayers were dried with MgSO₄ and evaporated to dryness to yield a darkslurry. The crude product was purified by column chromatography usingdichloromethane/hexane (1:2) as the eluent to afford the title productas a white solid (6.30 g, yield: 43%). ¹H NMR (400 MHz, CDCl₃) 7.84 (s,1H), 3.47 (d, 2H, J=7.2 Hz), 1.81 (m, 1H,), 1.40-1.15 (m, 24H), 0.85 (m,6H), ¹³C NMR (100 MHz, CDCl₃) δ 162.9, 161.3, 139.6, 137.8, 131.4, 74.6,43.1, 37.1, 32.16, 32.14, 31.7, 30.2, 29.88, 29.84, 29.79, 29.59, 29.54,26.51, 22.93, 22.92 (two peaks overlap), 14.38 ppm.

Synthesis of 1-Iodo-5-(2-octyldodecyl)thieno[3,4]pyrrole-4,6-dione (10)

A solution of 2-iodothiophene-3,4-dicarboxylic acid (10.26 g, 29.04mmol) in acetic anhydride (270 mL) was stirred at 75° C. over a periodof 2 hours. The solvent was removed and to the crude product was addeddioxane (250 mL), DMAP (3.56 g, 43.76 mmol) and 2-octyldodecan-1-amine(12.93 g, 43.46 mmol). The resulting solution was subsequently stirredat 55° C. over a period of 20 hours. Acetic anhydride (160 mL) was thenadded and the reaction mixture was stirred for an additional 4 hours at80° C. The reaction was subsequently quenched with water (300 mL) andwas extracted with dichloromethane (4×40 mL). The combined organiclayers were dried with MgSO₄ and evaporated to dryness to yield a darkslurry. The crude product was purified by column chromatography usingdichloromethane/hexane (1:2) as the eluent to afford the title productas a white solid (7.31 g, yield: 45%). ¹H NMR (400 MHz, CDCl₃) δ 7.84(s, 1H), 3.47 (d, 2H, J=7.2 Hz), 1.81 (m, 1H,), 1.40-1.15 (m, 28H), 0.85(m, 6H), ¹³C NMR (100 MHz, CDCl₃) δ 162.9, 161.3, 139.6, 137.8, 131.4,74.6, 43.1, 37.1, 32.16, 32.14, 31.7, 30.2, 29.88 (two peaks overlap),29.84 (two peaks overlap), 29.79 (two peaks overlap), 29.59 (two peaksoverlap), 29.54 (two peaks overlap), 26.51, 22.93, 22.92, 14.38 ppm.

Synthesis of 4,4″-didodecyl-2,2′:5′,2″-terthiophene (11)

2-(Tributylstannyl)-4-dodecylthiophene (0.75 g, 1.39 mmol) and2,5-dibromothiophene (0.12 g, 0.46 mmol) were dissolved in dry THF (5mL). The mixture was subsequently degassed. Pd₂dba₃ (0.016 g, 4% mol)and AsPh₃ (22 mg, 16% mol) were then added and the resulting mixturerefluxed over a period of 5 h. After cooling to room temperature, thesolvent was evaporated and the crude compound purified by columnchromatography (silica gel) using hexanes as the eluent. The product wasfurther purified by precipitation from cold acetone to afford the titleproduct as a light yellow solid (0.177 g, 65% yield). ¹H NMR (400 MHz,CDCl₃) δ 7.03 (s, 2H), 7.01 (s, 2H), 6.80 (s, 2H), 2.58 (t, 4H, J=7.8Hz), 1.66-1.57 (m, 4H), 1.37-1.17 (m, 36H), 0.89 (t, 6H, J=7.4 Hz), ¹³CNMR (100 MHz, CDCl₃) δ 144.40, 137.02, 136.56, 125.19, 124.14, 119.28,32.19, 30.76, 30.64, 29.93, 29.92, 29.91, 29.86, 29.73, 29.63, 29.57,22.96, 14.39.

Synthesis of 5,5″-dibromo-4,4″-didodecyl-2,2′:5′,2″-terthiophene (12)

4,4″-Didodecyl-2,2′:5′,2″-terthiophene (11) (0.147 g, 0.25 mmol) wasdissolved in a chloroform/acetic acid mixture (2:1) (9 mL) and cooled to0° C. NBS (0.090 g, 0.507 mmol) was added in one portion and thereaction mixture was subsequently stirred in the dark over a period of 1h at 0° C. The reaction was then quenched by adding water. The organicphase was separated and subsequently washed with a saturated NaOHsolution, dried over MgSO₄ and evaporated. The title product wasobtained as a yellow solid (0.171 g, 92%). ¹H NMR (400 MHz, CDCl₃) δ6.95 (s, 2H), 6.84 (s, 2H), 2.54 (t, 4H, J=7.7 Hz), 1.64-1.55 (m, 4H),1.39-1.18 (m, 36H), 0.89 (t, 6H, J=7.4 Hz); ¹³C NMR (100 MHz, CDCl₃) δ143.27, 136.57, 135.92, 124.70, 124.42, 108.18, 32.20, 29.96, 29.93,29.89, 29.84, 29.68, 29.64, 29.49, 22.98, 14.41.

Synthesis of N-(4-bromothiophenyl)-3-nonanamide (Scheme 12)

In a round bottom flask equipped with an addition funnel,2-azido-3-bromothiophene (4.0 g, 19.6 mmol) was dissolved in anhydrousTHF (160 mL). PySSPy (0.864 g, 3.92 mmol) and nonanoic acid (3.10 g,19.6 mmol) were then added to the solution. The mixture was subsequentlycooled to 0° C. and trimethylphosphine (60.4 mmol, 60.4 mL of a 1.0 Msolution in Toluene) was added dropwise to the solution at 0° C.Following the addition, the reaction mixture was stirred overnight atroom temperature. The reaction mixture was then extracted with asaturated solution of sodium bicarbonate and AcOEt. The organicfractions were dried over MgSO₄ and evaporated under reduced pressure.The crude product was purified by flash chromatography on silica using amixture of 90/10 hexane/AcOEt to obtain 4.92 g of the desired product aswhite powder (Yield: 79%). ¹H NMR (400 MHz, CDCl₃, ppm): δ 7.90 (d,J=3.6 Hz, 1H), 7.54 (s, 1H, NH); 7.22 (d, J=3.6 Hz, 1H), 2.41 (t, J=7.6Hz, 2H), 1.73 (m, 2H), 1.30 (m, 10H), 0.88 (t, J=7.0 Hz, 3H), ¹³C NMR(100 MHz, CDCl₃, ppm): δ 170.85; 132.77; 121.50; 110.59; 103.28; 37.45;32.06; 29.56; 29.45; 29.37; 25.75; 22.89; 14.35.

Synthesis of N-(4-bromothiophenyl)-3-nonanamide (Scheme 12)

In a round bottom flask equipped with a condenser,N-(4-bromothiophenyl)-3-nonanamide (5.25 g, 16.5 mmol) was dissolved inanhydrous THF (200 mL). Lawesson's reagent (10.0 g, 24.7 mmol) was thenadded to the solution. The reaction was refluxed overnight and thenextracted with AcOEt and a 10% NaOH solution. The organic fractions weredried over MgSO₄ and evaporated under reduced pressure. The crudeproduct was purified by flash chromatography on silica in a mixture of95/5 hexane/AcOEt to obtain 3.52 g of the desired product as a yellowoil (Yield: 64%). ¹H NMR (400 MHz, CDCl₃, ppm): δ 8.97 (d, J=3.6 Hz,1H), 7.26 (d, J=3.6 Hz, 1H), 2.84 (t, J=7.6 Hz, 2H), 1.84 (m, 2H), 1.26(m, 10H), 0.87 (t, J=7.0 Hz); ¹³C NMR (100 MHz, CDCl₃, ppm): δ 202.49;133.57; 121.52; 114.21; 104.96; 49.24; 31.85; 29.59; 29.35; 29.18;28.86; 22.69; 14.19.

Synthesis of 2-octylthieno[3,4-d]thiazole (Scheme 12)

In a round bottom flask equipped with a condenser,N-(4-bromothiophenyl)-3-nonanamide (3.5 g, 10.5 mmol) was dissolved inanhydrous THF (150 mL). Copper (I) iodide (0.100 g, 0.52 mmol),neocuproine (0.218 g, 1.05 mmol) and potassium carbonate (2.17 g, 15.7mmol) were then quickly added to the stirring solution. The reactionmixture was refluxed overnight and then extracted with AcOEt and water.The organic fractions were dried over MgSO₄ and evaporated under reducedpressure. The crude product was purified by flash chromatography onsilica in a mixture of 90/10 hexane/AcOEt to obtain 2.37 g of thedesired product as a yellow oil (Yield: 90%). ¹H NMR (400 MHz, CDCl₃,ppm): δ 7.45 (d, J=2.6 Hz, 1H), 7.16 (d, J=2.6 Hz, 1H), 2.98 (t, J=7.6Hz, 2H), 1.84 (m, 2H), 1.36 (m, 10H), 0.88 (t, J=7.0 Hz, 3H), ¹³C NMR(100 MHz, CDCl₃, ppm): δ 179.16; 160.17; 134.36; 109.97; 109.61; 35.59;32.05; 29.49; 29.37; 29.15; 22.89; 14.35.

Synthesis of 4,6-dibromo-2-octylthieno[3,4-d]thiazole (13) (Scheme 12)

To a solution of 2-octylthieno[3,4-d]thiazole (0.590 g, 23.3 mmol) inTHF (80 mL) was added n-bromosuccinimide (NBS) (0.870 g, 48.9 mmol). Thereaction mixture was allowed to stir at room temperature overnight. Thereaction mixture was then quenched with water, extracted with diethylether, dried with anhydrous MgSO₄ and concentrated under reducedpressure. The crude product was purified by flash chromatography using90/10 hexanes/AcOEt to obtain 0.743 g of the title compound as an orangeoil (Yield: 82%). ¹H NMR (400 MHz, CDCl₃, ppm): δ 2.97 (t, J=7.6 Hz,2H), 1.81 (m, 2H), 1.34 (m, 10H), 0.88 (t, J=7.0 Hz, 3H), ¹³C NMR (100MHz, CDCl₃, ppm): δ 180.69; 156.92; 135.91; 95.58; 94.49; 35.86; 32.02;29.44; 29.36; 29.32; 29.30; 22.88; 14.35.

Synthesis of 5-(9-heptadecanyl)-4H-thieno[3,4-c]pyrrole-4,6(5H)-dione

A solution of thiophene-3, 4-dicarboxylic acid (2.5 g, 14.52 mmol) inacetic anhydride (60 mL) was stirred for 4 h at 140° C. The reactionmixture was then concentrated to yield thiophene-3, 4-dicarboxylicanhydride as a brown solid which was used without further purification.The anhydride was dissolved in toluene (90 mL), followed by the additionof 9-heptadecanamine (3.7 g, 14.52 mmol). The reaction mixture wassubsequently refluxed overnight. The reaction mixture was then allowedto cool to room temperature and was subsequently concentrated. Thereaction mixture was dissolved in thionyl chloride (SOCl₂) (80 mL) andrefluxed over a period of 4.5 hours. The reaction mixture was cooled andconcentrated to dryness. The residue was purified by columnchromatography using methylene dichloride:hexanes (3:7) as the eluent toafford the title compound as a beige solid (2.2 g, Yield: 39%). ¹H NMR(400 MHz, CDCl3, ppm) δ: 7.78 (s, 2H), 4.10 (hept, 1H), 2.10-1.95 (m,2H), 1.71-1.60 (m, 2H), 1.33-1.18 (m, 24H), 0.85 (t, 6H), ¹³C NMR (100MHz, CDCl3, ppm) δ: 163.27, 136.69, 125.47, 52.95, 32.04, 29.67, 29.52,29.45, 26.89, 22.86, 14.32.

Synthesis of 5-(nonan-5-yl)-5H-thieno[3,4-c]pyrrole-4,6-dione

A solution of thiophene-3, 4-dicarboxylic acid (2.5 g, 14.52 mmol) inacetic anhydride (60 mL) was stirred for 4 h at 140° C. The reactionmixture was concentrated to yield thiophene-3, 4-dicarboxylic anhydrideas a brown solid which was used without further purification. Theanhydride was dissolved in toluene (90 mL), followed by the addition ofnonan-5-amine (2.08 g, 14.52 mmol). The reaction mixture wassubsequently refluxed overnight. The reaction mixture was then allowedto cool to room temperature and was subsequently concentrated. Theresulting mixture was dissolved in thionyl chloride (SOCl₂) (80 mL) andrefluxed over a period of 4.5 hours. The reaction mixture was cooleddown and concentrated to dryness. The residue was purified by columnchromatography using methylene dichloride:hexanes (3:7) as the eluent toafford the title compound as a beige solid (1.7 g, yield: 30%). ¹H NMR(400 MHz, CDCl3, ppm) δ: 7.73 (s, 2H), 4.02 (hept, 1H), 2.12-1.93 (m,2H), 1.63-1.51 (m, 2H), 1.26-1.04 (m, 12H), 0.72 (t, 6H), ¹³C NMR (100MHz, CDCl3, ppm) δ: 163.28, 136.69, 125.53, 52.98, 32.22, 29.05, 22.61,14.21.

Synthesis of Monomer 15

Monomer 14 (3.00 g, 10 mmol) and potassium carbonate (4.15 g, 30 mmol)were dissolved in 100 mL of dry DMF in a 250 mL three neck round bottomflask. The solution was heated to 50° C. and 1-bromo-2-octyldodecane(11.26 g, 30 mmol) was added dropwise over a period of 2 hours. Thereaction mixture was stirred at 80° C. for 48 hours. After reachingambient temperature, the reaction mixture was filtered under vacuumusing a 2 inch pad of silica to remove unreacted starting material. Achloroform portion was added and the organic phase was washed severaltimes with water (6×250 mL) to remove the residual DMF. The solvent wasdried using magnesium sulfate, filtered and then removed under reducedpressure to afford a crude purple product. Using a small silica gelcolumn, a drypack of the crude was flushed with methanol to removeimpurities. Further purification with a silica gel column usinghexanes:chloroform (8:1) as the eluent lead to the desired product (1.65g, 16% yield). M/Z calculated 860.6287 found 860.6278; ¹H NMR (CDCl₃,400 MHz, ppm) δ: 8.88 (d, J=3.4 Hz, 2H), 7.62 (d, J=4.8 Hz, 2H), 7.27(m, 2H), 4.01 (d, J=7.7 Hz, 4H), 1.90 (m, 2H), 1.21 (m, 64H), 0.87 (m,12H), ¹³C NMR (CDCl₃, 100 MHz, ppm) δ: 161.97, 140.65, 135.46, 130.69,130.07, 128.62, 108.15, 46.44, 37.96, 32.15, 32.11, 31.39, 31.17, 30.24,29.88, 29.87 (m), 29.79, 29.73, 29.59, 29.53, 26.43, 26.41, 22.93,22.90, 14.36, 14.35.

Synthesis of Monomer 16

Monomer 15 (1.30 g, 1.51 mmol) was dissolved in 30 mL of chloroform in a100 mL flask. After shielding the flask from light using an aluminumfoil, N-bromosuccinimide (0.56 g, 3.18 mmol) was added in portions andthe reaction mixture was left to stir overnight. The solution wasdropped in 100 mL of water and extracted with chloroform (3×50 mL). Thesolvent was subsequently dried using magnesium sulfate, filtered andthen removed under reduced pressure. A short silica plug usingchloroform as the eluent affords the desired compound as a purpleproduct (1.47 g, 95% yield). M/Z calculated 1016.4493 found 1016.4487;¹H NMR (CDCl₃, 400 MHz, ppm) δ: 8.63 (d, J=4.1 Hz, 2H), 7.21 (d, J=4.2Hz, 2H), 3.91 (d, J=7.6 Hz, 4H), 1.55 (s, 2H), 1.25 (m, 64H), 0.87 (m,12H), ¹³C NMR (CDCl₃, 100 MHz, ppm) δ: 161.61, 139.63, 135.55, 131.64,131.37, 119.17, 108.18, 46.56, 37.98, 32.16, 32.12, 31.38, 30.21, 29.88(m), 29.79, 29.73, 29.60, 29.53, 26.40, 22.93, 22.91, 14.37, 14.36.

Synthesis of Monomer 17

N-bromosuccinimide (317 mg, 1.78 mmol) was added in one portion to asolution of the dithienosilole substrate (399 mg, 0.89 mmol) in THF (6mL) and the reaction mixture stirred under an atmosphere of N₂ over aperiod of 1.5 hours. The reaction mixture was subsequently quenched withwater and extracted with dichloromethane (4×10 mL). The combinedextracts were washed with water, dried with anhydrous MgSO₄, filteredand the solvent removed in vacuo. The product was purified bychromatography (SiO₂, 5% Et₃N in hexanes) to provide a yellow solid,which was recrystallized in hexanes (267 mg, 73%). ¹H NMR (Acetone-d₆,399.78 MHz) δ: 2.21 (s, ¹J_(CH)=128.1 Hz, ²J_(SiH)=39.7 Hz, 6H, ArCH₃),0.42 (s, ¹J_(CH)=116.5 Hz, ²J_(SiH)=37.9 Hz, 6H, ArCH₃) ppm; ¹³C NMR(Acetone-d₆, 100.52 MHz) δ: 146.5, 142.3, 139.7, 108.4, 15.4 (ArCH₃),−4.8 ppm (SiCH₃).

Synthesis of Monomer 18

N-bromosuccinimide (78 mg, 0.44 mmol) was added in one portion to asolution of dithienosilole substrate (126 mg, 0.21 mmol) in THF (2.1 mL)and the reaction mixture stirred under an atmosphere of N2. The reactionwas monitored by TLC and an additional amount of NBS (4 mg, 0.021 mmol)was added after 20 hours. Following an additional 2 hours, the reactionmixture was quenched with water and extracted with hexanes (4×10 mL).The combined extracts were washed with water, dried with anhydrousMgSO₄, filtered and the solvent removed in vacuo. The product waspurified by chromatography (SiO₂, hexanes) to provide a yellow oil (114mg, 90%). ¹H NMR (Acetone-d₆, 499.92 MHz) δ: 2.28 (t, ¹J=3.2 Hz, 6H),1.27-0.73 (m, 34H), ppm, ¹³C NMR (Acetone-d₆, 125.72 MHz) δ: 147.2,143.6 (¹J_(SiC)=67.3 Hz), 140.0 (²J_(SiC)=3.6 Hz), 109.0 (²J_(SiC)=23.9Hz), 36.9, 36.1, 36.09, 22.6, 17.6, 16.0 (t, ¹J=6.8 Hz), 14.3, 11.24,11.2 Hz.

Synthesis of Monomer 29

2,5-Dibromonitrobenzene (15.0 g, 53.4 mmol) was mixed with potassiumcarbonate anhydrous (73.8 g, 534 mmol) in dry DMSO (80 mL) under anitrogen atmosphere. The reaction mixture was heated to 50° C. and asolution of diethylmalonate (44.3 g, 267 mmol) in DMSO (40 mL) was addeddropwise over a period of one hour. The reaction mixture was left toreact for 18 h after which it was extracted with diethyl ether and thecombined organic phases washed with water. After removal of thesolvents, the intermediate compound diethyl2-(4-bromo-2-nitrophenyl)malonate was obtained as a light yellow oilmixed with diethyl malonate as an impurity. This mixture was directlyused without further purification and was solubilized in a mixture ofwater (110 mL), sulfuric acid (110 mL) and ethanol (330 mL) and heatedto reflux. Zinc powder (35 g, 534 mmol) was then slowly added to thereaction mixture. The mixture was left to react over a period of onehour prior to the slow addition of a second portion of zinc powder (35g, 534 mmol). The reaction mixture was left to react for two hoursfollowed by it being transferred into water (1.5 L). The product wasleft to crystallize overnight after which it was filtered. The whitesolid obtained was washed with water to yield pure 6-bromooxindole (29)(9.75 g, yield=86%). M.P.=214-216° C., ¹H NMR (400 MHz, DMSO-d₆, ppm) δ:10.50 (s, 1H), 7.15 (d, J=8.0 Hz, 1H), 7.10 (dd, J¹=8.0 Hz, J²=1.8 Hz,1H), 6.94 (d, J=1.8 Hz, 1H), ¹³C NMR (100 MHz, DMSO-d₆, ppm) δ: 176.26,145.41, 126.21, 125.28, 123.66, 119.90, 111.86, 35.41; HRMS (ESI)(M+H)+:Calcd: 210.9633. Found: 210.9632.

Synthesis of Monomer 30

6-Bromooxindole (29) (5.14 g, 24.3 mmol) and commercially available6-bromoisatin (5.50 g, 24.3 mmol) were solubilised in acetic acid (160mL). Hydrochloric acid (12 M, 1.2 mL) was added and the mixture wasrefluxed over a period of 26 hours. The reaction mixture was thendropped into water (1 L) and filtered. The resulting brown solid waswashed with water, methanol and ethyl acetate and subsequentlytriturated in ethyl acetate for an hour (250 mL). The desired productwas obtained as a dark brown solid after filtration (9.24 g, 91%).M.P.=>400° C., ¹H NMR (400 MHz, DMSO-d₆, ppm) δ: 11.10 (s, 2H), 8.99 (d,J=8.8 Hz, 1H), 7.19 (dd, J¹=8.8 Hz, J²=1.9 Hz, 2H), 6.99 (d, J=1.9 Hz,2H), HRMS (ESI)(M+H)⁺: Calcd: 417.8953. Found: 417.8938.

Synthesis of Monomer 31

6,6′-Dibromoisoindigo (30) (3.65 g, 8.68 mmol) and anhydrous potassiumcarbonate (6.00 g, 43.4 mmol) were mixed in dry DMF (175 mL) and thereaction mixture heated to 100° C. under a nitrogen atmosphere.2-Hexyl-1-bromodecane (7.95 g, 26.0 mmol) was then added and theresulting red solution was left to react over a period of 22 hours. Thereaction mixture was then poured into water and extracted withdichloromethane. The combined organic phases were washed with brine,dried with sodium sulfate and subsequently evaporated under reducedpressure to yield the crude product as a red oil. The crude product waspurified over a short silica column using hexanes as a first eluent andthen a mixture of hexanes/dichloromethane (1:1) as a second eluent. Theresulting red oil solidified after several days. This product wasfurther purified by column chromatography over silica gel, first usingmethanol as the eluant to remove an oily by-product which could beobserved by thin film chromatography, and by further eluting withdichloromethane. Any residual silica was removed by solubilizing theproduct in dichloromethane followed by vacuum filtration. The desiredproduct was finally obtained as a red solid (6.21 g, yield=82%).M.P.=50-52° C., ¹H NMR (400 MHz, CDCl₃, ppm) δ: 9.06 (d, J=8.9 Hz, 2H),7.16 (dd, J¹=8.9 Hz, J²=1.5 Hz, 2H), 6.89 (d, J=1.5 Hz, 2H), 1.88 (d,J=7.3 2H), 3.74 (m, 1H), 1.85 (m, 2H), 1.2-1.4 (m, 48H), 0.86 (t, J=6.4Hz, 12H), ¹³C NMR (100 MHz, DMSO-d₆, ppm) δ: 168.08, 146.19, 132.54,131.06, 126.66, 125.08, 120.38, 111.51, 67.98, 44.68, 36.09, 31.88,31.91, 31.51, 29.99, 29.65, 29.55, 29.30, 26.37, 26.34, 22.67, 22.64,14.12, 14.09; HRMS (ESI)(M+H)⁺: Calcd: 866.3961. Found: 866.3935.

Synthesis of Polymers (P1-P4) by Direct Heteroarylation Polycondensation(n Varies Between 10-200)

Synthesis of P1

5-(2-hexyldecyl)-5H-thieno[3,4-c]pyrrole-4,6-dione (4) (94.4 mg, 0.25mmol), 5,5′-dibromo-4,4′-dioctyl-2,2′bithiophene (128.1 mg, 0.25 mmol),trans-di(μ-acetato)bis[o-(di-o-tolyl-phosphino)benzyl]dipalladium(II)(4.71 mg, 2% mol) (catalyst), ligand (7.04 mg, 8% mol) and Cs₂CO₃ (162.9mg 0.50 mmol) were put in a Biotage microwave vial (size 2 to 5 mL) witha magnetic stirring bar. The vial was sealed with a cap and then purgedwith nitrogen to remove the oxygen. Dry THF (1 mL; purged with N₂) wasadded and the reaction mixture was heated using an oil bath at 120° C.(reaction under pressure). At the end of the reaction time, the reactionmixture was cooled and the corresponding5-alkylthieno[3,4-c]pyrrole-4,6-dione (50 mg in 1 mL) was added as acapping agent. The solution was subsequently heated again at 120° C.over a period of 1 hour to complete the end-capping procedure. After anadditional hour of reaction time, the whole mixture was cooled to roomtemperature and poured into cold methanol (500 mL). The resultingprecipitate was filtered. Soxhlet extractions using acetone, followed byhexanes removed catalytic residues and low molecular weight materials.The polymers were then extracted with chloroform. The solvent wasreduced to about 10 mL and the mixture was poured into cold methanol.The resulting precipitate was filtered. P1 was obtained in 96% yield ofsoluble fraction in CHCl₃; M_(n) of 56 kDa.

Synthesis of P2

1-Iodo-5-(2-hexyldecyl)thieno[3,4]pyrrole-4,6-dione (9) (100.00 mg, 0.20mmol),trans-di(μ-acetato)bis[o-(di-o-tolyl-phosphino)benzyl]dipalladium(II)(3.71 mg, 2% mol) (catalyst), ligand (5.60 mg, 8% mol), Cs₂CO₃ (65.16 mg0.20 mmol) and silver acetate (33.30 mg, 0.20 mmol) were put in aBiotage microwave vial (size 2 to 5 mL) with a magnetic stirring bar.The vial was sealed with a cap and then purged with nitrogen to removethe oxygen. Dry THF (0.8 mL, purged with N₂) was added and the reactionmixture was heated using an oil bath at 120° C. (reaction underpressure). After 22 hours of reaction time, the reaction mixture wascooled and the corresponding 5-alkylthieno[3,4-c]pyrrole-4,6-dione (50mg in 1 mL) was added as a capping agent. The solution was subsequentlyheated again at 120° C. over a period of 1 hour to complete theend-capping procedure. After an additional hour of reaction time, thewhole mixture was cooled to room temperature and poured into coldmethanol (500 mL). The resulting precipitate was filtered. Soxhletextractions using acetone, followed by hexanes removed catalyticresidues and low molecular weight materials. The polymers were thenextracted with chloroform. The solvent was reduced to about 10 mL andthe mixture was poured into cold methanol. The resulting precipitate wasfiltered. P2 was obtained in 81% yield of soluble fraction in CHCl₃,M_(n) of 11 kDa.

Synthesis of P3

1-Iodo-5-(2-octyldodecyl)thieno[3,4]pyrrole-4,6-dione (10) (100.00 mg,0.18 mmol),trans-di(μ-acetato)bis[o-(di-o-tolyl-phosphino)benzyl]dipalladium(II)(3.34 mg, 2% mol) (catalyst), ligand (5.04 mg, 8% mol), Cs₂CO₃ (58.64 mg0.18 mmol) and silver acetate (29.97 mg, 0.18 mmol) were put in aBiotage microwave vial (size 2 to 5 mL) with a magnetic stirring bar.The vial was sealed with a cap and then purged with nitrogen to removethe oxygen. Dry THF (0.7 mL, purged with N₂) was added and the reactionmixture was heated using an oil bath at 120° C. (reaction underpressure). After 22 hours of reaction time, the reaction was cooled andthe corresponding 5-alkylthieno[3,4-c]pyrrole-4,6-dione (50 mg in 1 mL)was added as a capping agent. The solution was subsequently heated againat 120° C. over a period 1 hour to complete the end-capping procedure.After an additional hour of reaction time, the whole mixture was cooledto room temperature and poured into cold methanol (500 mL). Theresulting precipitate was filtered. Soxhlet extractions using acetone,followed by hexanes removed catalytic residues and low molecular weightmaterials. The polymers were then extracted with chloroform. The solventwas reduced to about 10 mL and the mixture was poured into coldmethanol. The resulting precipitate was filtered. P3 was obtained in 55%yield of soluble fraction in CHCl₃; M_(n) of 23 kDa.

Synthesis of P4

5-(tetradecyl)-5H-thieno[3,4-c]pyrrole-4,6-dione (41.86 mg, 0.121 mmol),5,5″-dibromo-4,4″-didodecyl-2,2′:5′,2″-terthiophene (90 mg, 0.121 mmol),trans-di(μ-acetato)bis[o-(di-o-tolyl-phosphino)benzyl]dipalladium(II)(2.28 mg, 2% mol) (catalyst), tris(o-methoxyphenyl)phosphine (3.41 mg,8% mol) (ligand) and 052003 (79 mg 0.242 mmol) were put in a Biotagemicrowave vial (size 2-5 mL) with a magnetic stirring bar. The vial wassealed with a cap and then purged with nitrogen to remove the oxygen.Dry THF (0.5 mL, purged with N₂) was added and the reaction was heatedwith an oil bath at 120° C. (reaction under pressure) over a period of20 h. After cooling to room temperature, the reaction mixture was pouredinto cold methanol (200 mL). The resulting precipitate was filtered.Soxhlet extractions using acetone followed by hexanes removed catalyticresidues and low molecular weight materials. The polymers were thenextracted with chloroform. The solvent was reduced to about 10 mL andthe mixture was poured into cold methanol. P4 was obtained in 49% yieldof soluble fraction in CHCl₃; M_(n) of 15 kDa.

Synthesis of P1*

The experimental conditions were those as previously reported by Wei etal. for similar copolymers.^([9])1,3-Dibromo-5-(2-hexyldecyl)-5H-thieno[3,4-c]pyrrole-4,6-dione (8) (74.7mg, 0.140 mmol),4,4′-dioctyl-5,5′-bis(trimethylstannyl)-2,2′-bithiophene (7) (100.0 mg,0.140 mmol), Pd₂(dba)₃ (2.6 mg, 2% mol), and P(o-Tolyl)₃ (6.8 mg, 16%)were put in a 15 mL round bottom flask which was subsequently purgedwith N2. Dry chlorobenzene (5 mL, purged with N₂) was added and themixture was stirred at 130° C. over a period of 48 h. Bromobenzene wasthen added to the reaction mixture followed by the addition oftrimethylphenyltin as capping agent one hour later. After an additionalhour of reaction time, the reaction mixture was cooled to roomtemperature and poured into cold methanol (500 mL). The resultingprecipitate was filtered. Soxhlet extractions using acetone, followed byhexanes removed catalytic residues and low molecular weight materials.The polymers were then extracted with chloroform. The solvent wasreduced to about 30 mL and the mixture was poured into cold methanol.P1* was obtained in 71% yield of soluble fraction in CHCl₃; M_(n) of 9kDa.

Synthesis of PCTPD by Direct Arylation Polycondensation (n VariesBetween 10-200)

Poly[N-9-heptadecanyl-2,7-carbazole, 3-thiophene-5-octylthieno [3,4-c]pyrrole-4,6-dione] (PCTPD) was synthesized by direct arylation asfollows: 5-(2-octyl)-5H-thieno[3,4-c]pyrrole-4,6-dione (94.4 mg, 0.25mmol), N-9-heptadecanyl-2,7-dibromocarbazole (128.1 mg, 0.25 mmol),palladium acetate (catalyst, 5% mol), tris(2-methoxyphenyl)phosphine(ligand, 15.0% mol) and 052003 (162.9 mg 0.50 mmol) were added to aBiotage microwave vial (2-5 mL) with a magnetic stirring bar. The vialwas sealed with a cap and then purged with nitrogen to remove theoxygen. Dry THF (1 mL; purged with N₂) was added and the reactionmixture was heated using an oil bath at 120° C. (reaction underpressure). After 48 hours of reaction time, the reaction mixture wascooled and the corresponding 5-alkylthieno[3,4-c]pyrrole-4,6-dione wasadded as a capping agent. The solution was subsequently heated again at120° C. over a period of 1 hour to complete the end-capping procedure.After an additional hour of reaction time, the whole mixture was cooledto room temperature and poured into cold methanol (500 mL). Theprecipitate was filtered using a 0.45

m nylon filter. Soxhlet extractions using acetone, followed by hexanesremoved catalytic residues and low molecular weight materials. Thepolymers were then extracted with chloroform. The solvent was reduced toabout 30 mL and the mixture was poured into cold methanol. The resultingpurified polymer (dark-red) was obtained in 78% yield (130 mg) followingvacuum-drying at 80° C. overnight. ¹H NMR (400 MHz, CDCl₃, ppm) δ: 8.98(br, 1H), 8.81 (br, 1H), 8.15 (br, 2H), 7.81 (br, 2H), 4.87 (br, 1H),3.80 (br, 2H), 2.61 (br, 2H), 2.14 (br, 2H), 1.72 (br, 4H), 1.15-1.31(br, 31H), 0.79 (br, 9H). M _(n)=34 kg/mol, M _(w)=44 kg/mol,polydispersity=1.3.

Synthesis of P5 (Stille cross-coupling);poly[2,6-(4,8-bis-(ethylhexyl-oxyl)benzo[1,2-b:4,5-b′]dithiophene)-alt-4,6-(2-n-octyl)thieno(4,4-d]thiazole]

In a 25 mL flask fitted with a condenser were added2,6-bis(trimethyltin)-4,8-di(ethylhexyl-oxyl)benzo[1,2-b:4,5-b]dithiophene(0.392 g, 0.508 mmol), 2-octyl-4,6-dibromo-thieno[3,4-d]thiazole (0.209g, 0.508 mmol), Pd₂dba₃ (9.3 mg, 0.0102 mmol), AsPh₃ (12.5 mg, 0.0406mmol), degassed toluene (0.5 mL) and degassed DMF (0.5 mL). The reactionmixture was vigorously stirred for 48 h at 110° C. After reactioncompletion, bromobenzene (5.3 μL, 0.05 mmol) was added, followed by theaddition of trimethyl(phenyl)tin (one hour later) (9.1 μL, 0.05 mmol)and the reaction mixture heated for an additional hour. The reactionmixture was then cooled to room temperature and the polymer precipitatedin methanol, filtered through a 0.45 μm nylon filter and washed using aSoxhlet apparatus with acetone, hexanes and then chloroform. Thechloroform fraction was subsequently reduced to 20-30 mL and thenprecipitated in methanol, filtered through a 0.45 μm nylon filter andair-dried to give 0.341 g of the desired polymer. (Yield: 97%).

Synthesis of P5 (Direct Arylation);poly[2,6-(4,8-bis-(ethylhexyl-oxyl)benzo[1,2-b:4,5-b′]dithiophene)-alt-4,6-(2-n-octyl)thieno[4,4-d]thiazole]

2,6-Dibromo-4,8-di(ethylhexyl-oxyl)benzo[1,2-b:4,5-b′]dithiophene (0.192g, 0.318 mmol), 2-octylthieno[3,4-d]thiazole (0.0805 g, 0.318 mmol),trans-di(μ-acetato)bis[o-(di-o-tolyl-phosphino)benzyl]dipalladium(II)(5.9 mg, 2% mol), pivalic acid (9.7 mg, 30% mol),tris(2-methoxyphenyl)phosphine (9.05 mg, 8% mol) and cesium carbonate(238.0 mg 0.73 mmol) were put in a Biotage microwave vial (size 2 to 5mL) equipped with a magnetic stirring bar. The vial was sealed with acap and then purged with nitrogen to remove any oxygen. Toluene (2.1 mL)was added and the reaction mixture was heated with an oil bath at 120°C. (reaction under pressure) for 24 h. The reaction mixture was thencooled to room temperature and the polymer precipitated in methanol,filtered through a 0.45 μm nylon filter and washed using a Soxhletapparatus with acetone, hexanes and then chloroform. The chloroformfraction was subsequently reduced to 20-30 mL and then precipitated inmethanol, filtered through a 0.45 μm nylon filter and air-dried to give0.111 g of the desired polymer. (Yield: 50%).

Synthesis of P6;poly[4,6-(2-octylthieno[3,4-d]thiazole)-alt-1,3-(5-(heptadecan-9-yl)-5H-thieno[3,4-c]pyrrole-4,6-dione)]

5-(Heptadecan-9-yl)-5H-thieno[3,4-c]pyrrole-4,6-dione (0.150 g, 0.38mmol), 2-octyl-4,6-dibromo-thieno[3,4-d]thiazole (0.157 g, 0.38 mmol),trans-di(μ-acetato)bis[o-(di-o-tolyl-phosphino)benzyl]dipalladium(II)(7.2 mg, 2% mol), pivalic acid (11.7 mg, 30% mol),tris(2-methoxyphenyl)phosphine (10.7 mg, 4% mol) and cesium carbonate(250.0 mg 0.76 mmol) were put in a Biotage microwave vial (size 2 to 5mL) equipped with a magnetic stirring bar. The vial was sealed with acap and then purged with nitrogen to remove any oxygen. THF (1.5 mL) wasadded and the reaction was heated with using oil bath at 120° C.(reaction under pressure) for 24 h. The reaction mixture was then cooledto room temperature and the polymer precipitated in methanol, filteredthrough a 0.45 μm nylon filter and washed using a Soxhlet apparatus withacetone, hexanes and then chloroform. The chloroform fraction wasreduced to 20-30 mL and then precipitated in methanol, filtered througha 0.45 μm nylon filter and air-dried to give 0.100 g of the desiredpolymer. (Yield: 77%).

Synthesis of P7;poly[4,6-(2-octylthieno[3,4-d]thiazole)-alt-3,6-bis(thiophen-5-yl)-2,5-bis(2-octyldodecyl)pyrrolo[3,4-c]pyrrole-1,4(2H,5H)-dione]

3,6-bis(5-bromothiophen-2-yl)-2,5-bis(2-octyldodecyl)pyrrolo[3,4-c]pyrrole-1,4(2H,5H)-dione(0.112 g, 0.109 mmol), 2-octylthieno[3,4-d]thiazole, (0.028 g, 0.109mmol),trans-di(μ-acetato)bis[o-(di-o-tolyl-phosphino)benzyl]dipalladium(II)(1.8 mg, 2% mol), pivalic acid (3.1 mg, 30% mol),tris(2-methoxyphenyl)phosphine (2.8 mg, 4% mol) and cesium carbonate(74.9 mg 0.4 mmol) were put in a Biotage microwave vial (size 2 to 5 mL)equipped with a magnetic stirring bar. The vial was sealed with a capand then purged with nitrogen to remove any oxygen. THF (1 mL) was addedand the reaction mixture was heated using oil bath at 120° C. (reactionunder pressure) for 24 h. The reaction mixture was subsequently cooledto room temperature and the polymer precipitated in methanol, filteredthrough a 0.45 μm nylon filter and washed using a Soxhlet apparatus withacetone, hexanes and then chloroform. The chloroform fraction wasreduced to 20-30 mL and then precipitated in methanol, filtered througha 0.45 μm nylon filter and air-dried to give 0.072 g of the desiredpolymer. (Yield: 60%).

Synthesis of P9

5-(Tetradecyl)-5H-thieno[3,4-c]pyrrole-4,6-dione (41.86 mg, 0.121 mmol),5,5″-dibromo-4,4″-didodecyl-2,2′:5′,2″-terthiophene (90 mg, 0.121 mmol),trans-di(μ-acetato)bis[o-(di-o-tolyl-phosphino)benzyl]dipalladium(II)(2.28 mg, 4% mol), tris(o-methoxyphenyl)phosphine (3.41 mg, 8% mol) andCs₂CO₃ (79 mg 0.242 mmol) were added in a Biotage microwave vial (2-5mL) equipped with a magnetic stirring bar. The vial was sealed with acap and then purged with nitrogen to remove any oxygen. THF (0.5 mL) wasadded and the reaction mixture was heated using an oil bath at 120° C.(reaction under pressure) for 20 h. The reaction mixture was then cooledto room temperature and the polymer precipitated by pouring the mixtureinto cold methanol (200 mL). The precipitate was subsequently filtered.Soxhlet extractions with acetone followed by hexanes removed catalyticresidues and low molecular weight materials. Polymers were thenextracted with chloroform. The solvent was reduced to about 10 mL andthe mixture was poured into cold methanol. P9 was obtained in 49% yieldof soluble fraction in CHCl₃ (M_(n) of 10 kDa, M_(w)=16 kDa, PDI=1.52).

Synthesis of P10

5-(Octyl)-5H-thieno[3,4-c]pyrrole-4,6-dione (32.1 mg, 0.121 mmol),5,5″-dibromo-4,4″-didodecyl-2,2′:5′,2″-terthiophene (90 mg, 0.121 mmol),trans-di(μ-acetato)bis[o-(di-o-tolyl phosphino)benzyl]dipalladium(II)(2.28 mg, 4% mol), tris(o-methoxyphenyl)phosphine (3.41 mg, 8% mol) andCs₂CO₃ (79 mg 0.242 mmol) were added in a Biotage microwave vial (2-5mL) equipped with a magnetic stirring bar. The vial was sealed with acap and then purged with nitrogen to remove any oxygen. THF (0.5 mL) wasadded and the reaction mixture was heated using an oil bath at 120° C.(reaction under pressure) for 20 h. The reaction mixture was then cooledto room temperature and the polymer precipitated by pouring the mixtureinto cold methanol (200 mL). The precipitate was subsequently filtered.Soxhlet extractions with acetone followed by hexanes removed catalyticresidues and low molecular weight materials. Polymers were thenextracted with chloroform. The solvent was reduced to about 10 mL andthe mixture was poured into cold methanol. P10 was obtained in 49% yieldof soluble fraction in CHCl₃ (M_(n) of 10 kDa, M_(w)=13.6 kDa,PDI=1.31).

Synthesis of P11

5-(9-Heptadecanyl)-4H-thieno[3,4-c]pyrrole-4,6-dione (118.5 mg, 0.303mmol), 5,5′-dibromo-4,4′-didodecyl-2,2′-bithiophene (200 mg, 0.303mmol),trans-di(μ-acetato)bis[o-(di-o-tolyl-phosphino)benzyl]dipalladium(II)(5.8 mg, 4% mol), tris(o-methoxyphenyl)phosphine (8.5 mg, 8% mol) andCs₂CO₃ (197 mg 0.61 mmol) were added in a Biotage microwave vial (2-5mL) equipped with a magnetic stirring bar. The vial was sealed with acap and then purged with nitrogen to remove any oxygen. THF (1.25 mL)was added and the reaction mixture was heated using an oil bath at 120°C. (reaction under pressure) for 22 h. The reaction mixture was thencooled to room temperature and the polymer precipitated by pouring themixture into cold methanol (300 mL). The precipitate was subsequentlyfiltered. Soxhlet extractions with acetone followed by hexanes removedcatalytic residues and low molecular weight materials. Polymers werethen extracted with chloroform. The solvent was reduced to about 10 mLand the mixture was poured into cold methanol. P11 was obtained in 94%yield of soluble fraction in CHCl₃ (M_(n) of 48 kDa, M_(w)=110 kDA,PDI=2.3).

Synthesis of P12

5-(2-Ethylhexyl)-5H-thieno[3,4-c]pyrrole-4,6-dione (32.13 mg, 0.121mmol), 5,5″-dibromo-4,4″-didodecyl-2,2′:5′,2″-terthiophene (90 mg, 0.121mmol), trans-di(μ-acetato)bis[o-(di-o-tolylphosphino)benzyl]dipalladium(II) (2.28 mg, 4% mol),tris(o-methoxyphenyl)phosphine (3.41 mg, 8% mol) and Cs₂CO₃ (79 mg 0.242mmol) were added in a Biotage microwave vial (2-5 mL) equipped with amagnetic stirring bar. The vial was sealed with a cap and then purgedwith nitrogen to remove any oxygen. THF (0.5 mL) was added and thereaction mixture was heated using an oil bath at 120° C. (reaction underpressure) for 20 h. The reaction mixture was then cooled to roomtemperature and the polymer precipitated by pouring the mixture intocold methanol (200 mL). The precipitate was subsequently filtered.Soxhlet extractions with acetone followed by hexanes removed catalyticresidues and low molecular weight materials. Polymers were thenextracted with chloroform. The solvent was reduced to about 10 mL andthe mixture was poured into cold methanol. P12 was obtained in 35% yieldof soluble fraction in CHCl₃ (M_(n) of 9.7 kDa, M_(w)=12.6 kDa,PDI=1.3).

Synthesis of P13

5(2-Octyldodecyl)thieno[3,4]pyrrole-4,6-dione (52.51 mg, 0.121 mmol),5,5″-dibromo-4,4″-didodecyl-2,2′:5′,2″-terthiophene (90 mg, 0.121 mmol),trans-di(μ-acetato)bis[o-(di-o-tolyl phosphino)benzyl]dipalladium(II)(2.28 mg, 4% mol), tris(o-methoxyphenyl)phosphine (3.41 mg, 8% mol) andCs₂CO₃ (79 mg 0.242 mmol) were added in a Biotage microwave vial (2-5mL) equipped with a magnetic stirring bar. The vial was sealed with acap and then purged with nitrogen to remove any oxygen. THF (0.5 mL) wasadded and the reaction mixture was heated with an oil bath at 120° C.(reaction under pressure) for 20 h. The reaction mixture was then cooledto room temperature and the polymer precipitated by pouring the mixtureinto cold methanol (200 mL). The precipitate was subsequently filtered.Soxhlet extractions with acetone followed by hexanes removed catalyticresidues and low molecular weight materials. Polymers were thenextracted with chloroform. The solvent was reduced to about 10 mL andthe mixture was poured into cold methanol. P13 was obtained in 80% yieldof soluble fraction in CHCl₃ (M_(n) of 32 kDa, M_(w)=65.3 kDa,PDI=2.04).

Synthesis of P14

5-(Nonan-5-yl)-5H-thieno[3,4-c]pyrrole-4,6-dione (67.7 mg, 0.242 mmol),5,5″-dibromo-4,4″-didodecyl-2,2′:5′,2″-terthiophene (180 mg, 0.242mmol), trans-di(μ-acetato)bis[o-(di-o-tolylphosphino)benzyl]dipalladium(II) (4.56 mg, 4% mol),tris(o-methoxyphenyl)phosphine (6.82 mg, 8% mol), Cs₂CO₃ (158 mg 0.484mmol) and pivalic acid (7 mg, 30% mol) were added in a Biotage microwavevial (2-5 mL) equipped with a magnetic stirring bar. The vial was sealedwith a cap and then purged with nitrogen to remove any oxygen. THF (1.0mL) was added and the reaction mixture was heated using an oil bath at120° C. (reaction under pressure) for 15 h. The reaction mixture wasthen cooled to room temperature and the polymer precipitated by pouringthe mixture into cold methanol (200 mL). The precipitate wassubsequently filtered. Soxhlet extractions with acetone followed byhexanes removed catalytic residues and low molecular weight materials.Polymers were then extracted with chloroform. The solvent was reduced toabout 10 mL and the mixture was poured into cold methanol. P14 wasobtained in 80% yield of soluble fraction in CHCl₃ (M_(n) of 18 kDa,M_(w)=45 kDa, PDI=2.5).

Synthesis of P15

5-(9-Heptadecanyl)-4H-thieno[3,4-c]pyrrole-4,6(5H)-dione (118.5 mg,0.303 mmol), 5,5′-dibromo-4,4′-didodecyl-2,2′-bithiophene (200 mg, 0.303mmol),trans-di(μ-acetato)bis[o-(di-o-tolyl-phosphino)benzyl]dipalladium(II)(5.8 mg, 4% mol), tris(o-methoxyphenyl)phosphine (8.5 mg, 8% mol) and052003 (197 mg 0.61 mmol) were added in a Biotage microwave vial (2-5mL) equipped with a magnetic stirring bar. The vial was sealed with acap and then purged with nitrogen to remove any oxygen. THF (1.25 mL)was added and the reaction mixture was heated with an oil bath at 120°C. (reaction under pressure) for 22 h. The reaction mixture was thencooled to room temperature and the polymer precipitated by pouring themixture into cold methanol (300 mL). The precipitate was subsequentlyfiltered. Soxhlet extractions with acetone followed by hexanes removedcatalytic residues and low molecular weight materials. Polymers werethen extracted with chloroform. The solvent was reduced to about 10 mLand the mixture was poured into cold methanol. P15 was obtained in 94%yield of soluble fraction in CHCl₃ (M_(n) of 50 kDa, M_(w)=103 kDa,PDI=2.06).

Synthesis of P16

5-(9-Heptadecanyl)-4H-thieno[3,4-c]pyrrole-4,6(5H)-dione (107.7 mg,0.273 mmol), 5,5′-dibromo-4,4′-dioctyl-2,2′-bithiophene (150 mg, 0.273mmol),trans-di(μ-acetato)bis[o-(di-o-tolyl-phosphino)benzyl]dipalladium(II)(5.6 mg, 4% mol), tris(o-methoxyphenyl)phosphine (8.2 mg, 8% mol) andCs₂CO₃ (180 mg 0.546 mmol) were added in a Biotage microwave vial (2-5mL) equipped with a magnetic stirring bar. The vial was sealed with acap and then purged with nitrogen to remove any oxygen. THF (1.22 mL)was added and the reaction mixture was heated using an oil bath at 120°C. (reaction under pressure) for 22 h. The reaction mixture was thencooled to room temperature and the polymer precipitated by pouring themixture into cold methanol (300 mL). The precipitate was subsequentlyfiltered. Soxhlet extractions with acetone followed by hexanes removedcatalytic residues and low molecular weight materials. Polymers werethen extracted with chloroform. The solvent was reduced to about 10 mLand the mixture was poured into cold methanol. P16 was obtained in 94%yield of soluble fraction in CHCl₃ (M_(n) of 47 kDa, M_(w)=98 kDa,PDI=2.08).

Synthesis of P17

5-(2-Octyldodecyl)thieno[3,4]pyrrole-4,6-dione (108.4 mg, 0.25 mmol),2,5-dibromothiophene (60.48 mg, 0.25 mmol),trans-di(μ-acetato)bis[o-(di-o-tolyl phosphino)benzyl]dipalladium(II) (5mg, 4% mol), tris(o-methoxyphenyl)phosphine (7.3 mg, 8% mol) and Cs₂CO₃(170 mg 0.5 mmol) were added in a Biotage microwave vial (2-5 mL)equipped with a magnetic stirring bar. The vial was sealed with a capand then purged with nitrogen to remove any oxygen. THF (1.2 mL) wasadded and the reaction mixture was heated using an oil bath at 120° C.(reaction under pressure) for 20 h. The reaction mixture was then cooledto room temperature and the polymer precipitated by pouring the mixtureinto cold methanol (200 mL). The precipitate was subsequently filtered.Soxhlet extractions with acetone followed by hexanes removed catalyticresidues and low molecular weight materials. Polymers were thenextracted with chloroform. The solvent was reduced to about 10 mL andthe mixture was poured into cold methanol. P17 was obtained in 71% yieldof soluble fraction in CHCl₃ (M_(n) of 13 kDa, M_(w)=20.8 kDa, PDI=1.6).

Synthesis of P18

5-(9-Heptadecanyl)-4H-thieno[3,4-c]pyrrole-4,6(5H)-dione (97.9 mg, 0.25mmol), 2,5-dibromothiophene (60.48 mg, 0.25 mmol),trans-di(μ-acetato)bis[o-(di-o-tolyl phosphino)benzyl]dipalladium(II) (5mg, 4% mol), tris(o-methoxyphenyl)phosphine (7.3 mg, 8% mol) and Cs₂CO₃(170 mg 0.5 mmol) were added in a Biotage microwave vial (2-5 mL)equipped with a magnetic stirring bar. The vial was sealed with a capand then purged with nitrogen to remove any oxygen. THF (1.2 mL) wasadded and the reaction mixture was heated using an oil bath at 120° C.(reaction under pressure) for 16 h. The reaction mixture was then cooledto room temperature and the polymer precipitated by pouring the mixtureinto cold methanol (200 mL). The precipitate was subsequently filtered.Soxhlet extractions with acetone followed by hexanes removed catalyticresidues and low molecular weight materials. Since the desired polymerswere substantially insoluble in chloroform, the residue was extractedwith hot o-dichlorobenzene. The solvent was reduced to about 10 mL andthe mixture was poured into cold methanol. P18 was obtained in 52% yield(M_(n) of 15.9 kDa, M_(w)=41.2 kDa, PDI=2.59).

Synthesis of P19

5-(Octyl)-5H-thieno[3,4-c]pyrrole-4,6-dione (93.5 mg, 0.352 mmol),2,6-dibromo-4,8-bis[(2-ethylhexyl)oxy]-benzo[1,2-b:4,5-b′]dithiophene(213 mg, 0.352 mmol), trans-di(μ-acetato)bis[o-(di-o-tolylphosphino)benzyl]dipalladium(II) (6.6 mg, 4% mol),tris(o-methoxyphenyl)phosphine (10 mg, 8% mol), Cs₂CO₃ (340 mg 0.71mmol) and pivalic acid (13 mg, 30% mol) were added in a Biotagemicrowave vial (2-5 mL) equipped with a magnetic stirring bar. The vialwas sealed with a cap and then purged with nitrogen to remove anyoxygen. Toluene (2.5 mL) was added and the reaction mixture was heatedusing an oil bath at 120° C. (reaction under pressure) for 24 h. Thereaction mixture was then cooled to room temperature and the polymerprecipitated by pouring the mixture into cold methanol (200 mL). Theprecipitate was subsequently filtered. Soxhlet extractions with acetonefollowed by hexanes removed catalytic residues and low molecular weightmaterials. Since the desired polymers were substantially insoluble inchloroform, the residue was extracted with hot o-dichlorobenzene. Thesolvent was reduced to about 10 mL and the mixture was poured into coldmethanol. P19 was obtained in 75% yield (M_(n) of 50.8 kDa, M_(w)=144.6kDa, PDI=2.85).

Synthesis of P20

5-(Octyl)-5H-thieno[3,4-c]pyrrole-4,6-dione (126.4 mg, 0.476 mmol),2,6-dibromo-4,8-bis(2-ethylhexyl) 4H-silolo[3,2-b:4,5-b′]dithiophene(274.7 mg, 0.476 mmol), trans-di(μ-acetato)bis[o-(di-o-tolylphosphino)benzyl]dipalladium(II) (8.9 mg, 4% mol),tris(o-methoxyphenyl)phosphine (13.7 mg, 8% mol), Cs₂CO₃ (505 mg 0.97mmol) and pivalic acid (17 mg, 30% mol) were added in a Biotagemicrowave vial (2-5 mL) equipped with a magnetic stirring bar. The vialwas sealed with a cap and then purged with nitrogen to remove anyoxygen. Toluene (2.15 mL) was added and the reaction mixture was heatedusing an oil bath at 120° C. (reaction under pressure) for 23 h. Thereaction mixture was then cooled to room temperature and the polymerprecipitated by pouring the mixture into cold methanol (200 mL). Theprecipitate was subsequently filtered. Soxhlet extractions with acetonefollowed by hexanes removed catalytic residues and low molecular weightmaterials. Polymers were then extracted with chloroform. The solvent wasreduced to about 10 mL and the mixture was poured into cold methanol.P20 was obtained in 55% yield (M_(n) of 21.2 kDa, M_(w)=66.6 kDa,PDI=3.14).

Synthesis of P21

1,3-Di(5′-bromo-3-octylthien-2′-yl)-5-octylthieno[3,4-c]pyrrole-4,6-dione(203.0 mg, 0.25 mmol), 5-octyl-thieno[3,4-c]pyrrole-4,6-dione (66.3 mg,0.25 mmol),trans-di(μ-acetato)bis[o-(di-o-tolyl-phosphino)benzyl]dipalladium(II)(4.71 mg, 2% mol), tri-tert-butylphosphonium tetrafluoroborate (5.8 mg,8% mol) and Cs₂CO₃ (162.9 mg 0.50 mmol) were put in a Biotage microwavevial (size 2 to 5 mL) equipped with a magnetic stirring bar. The vialwas sealed with a cap and then purged with nitrogen to remove anyoxygen. THF (1.0 mL) was added and the reaction mixture was heated usingan oil bath at 120° C. (reaction under pressure) for 24 h. The reactionmixture was then cooled to room temperature and the polymer precipitatedby pouring the mixture into cold methanol (500 mL). The precipitate wassubsequently filtered. Soxhlet extractions with acetone followed byhexanes removed catalytic residues and low molecular weight materials.Polymers were then extracted with chloroform. The solvent was reduced toabout 10 mL and the mixture was poured into cold methanol. P21 wasobtained in 96% yield of soluble fraction in CHCl₃.

Synthesis of P22

1-Iodo-5-(alkyl)thieno[3,4]pyrrole-4,6-dione (0.18 mmol),trans-di(μ-acetato)bis[o-(dio-tolyl-phosphino)benzyl]dipalladium(II)(3.34 mg, 4% mol), ligand (5.04 mg, 8% mol), Cs₂CO₃ (58.64 mg, 0.18mmol) and silver acetate (29.97 mg, 0.18 mmol) were added in a Biotagemicrowave vial (size 2 to 5 mL) equipped with a magnetic stirring bar.The vial was sealed with a cap and then purged with nitrogen to removeany oxygen. THF (0.7 mL) was added and the reaction mixture was heatedusing an oil bath at 120° C. (reaction under pressure) for 22 h. Thereaction mixture was then cooled and the corresponding5-alkylthieno[3,4-c]pyrrole-4,6-dione (50 mg in 1 mL) was added as acapping agent. The solution was subsequently heated again at 120° C.over a period of 1 hour to complete the end-capping procedure. After anadditional hour of reaction time, the whole mixture was cooled to roomtemperature and poured into cold methanol (500 mL). The resultingprecipitate was filtered. Soxhlet extractions with acetone followed byhexanes removed catalytic residues and low molecular weight materials.Polymers were then extracted with chloroform. The solvent was reduced toabout 10 mL and the mixture was poured into cold methanol. The resultingprecipitate was filtered to yield P22.

Synthesis of P23-24

1-Bromo-5-(alkyl)thieno[3,4]pyrrole-4,6-dione (0.18 mmol),trans-di(μ-acetato)bis[o-(dio-tolyl-phosphino)benzyl]dipalladium(II)(3.34 mg, 4% mol), ligand (5.04 mg, 8% mol) and KOAc (58.64 mg, 0.18mmol) were added in a Biotage microwave vial (size 2 to 5 mL) equippedwith a magnetic stirring bar. The vial was sealed with a cap and thenpurged with nitrogen to remove any oxygen. THF (0.7 mL) was added andthe reaction mixture was heated using an oil bath at 120° C. (reactionunder pressure) for 22 h. The reaction mixture was then cooled and thecorresponding 5-alkylthieno[3,4-c]pyrrole-4,6-dione (50 mg in 1 mL) wasadded as a capping agent. The solution was subsequently heated again at120° C. over a period of 1 hour to complete the end-capping procedure.After an additional hour of reaction time, the whole mixture was cooledto room temperature and poured into cold methanol (500 mL). Theresulting precipitate was filtered. Soxhlet extractions with acetonefollowed by hexanes removed catalytic residues and low molecular weightmaterials. Polymers were then extracted with chloroform. The solvent wasreduced to about 10 mL and the mixture was poured into cold methanol.The resulting precipitate was filtered to yield P22 or P23.

Synthesis of P25-28

5-alkylthieno[3,4-c]pyrrole-4,6-dione (0.25 mmol),1,3-dibromo-5-alkylthieno[3,4-c]pyrrole-4,6-dione (0.25 mmol),trans-di(μ-acetato)bis[o-(dio-tolyl-phosphino)benzyl]dipalladium(II) (4%mol), ligand (8% mol) and potassium acetate (0.50 mmol) were added in aBiotage microwave vial (size 2 to 5 mL) equipped with a magneticstirring bar. The vial was sealed with a cap and then purged withnitrogen to remove any oxygen. THF (1.0 mL) was added and the reactionmixture was heated with an oil bath at 120° C. (reaction under pressure)for 24 h. The reaction mixture was then cooled and the corresponding5-alkylthieno[3,4-c]pyrrole-4,6-dione (50 mg in 1 mL) was added as acapping agent. The solution was subsequently heated again at 120° C.over a period of 1 hour to complete the end-capping procedure. After anadditional hour of reaction time, the whole mixture was cooled to roomtemperature and poured into cold methanol (500 mL). The resultingprecipitate was filtered. Soxhlet extractions with acetone followed byhexanes removed catalytic residues and low molecular weight materials.Polymers were then extracted with chloroform. The solvent was reduced toabout 10 mL and the mixture was poured into cold methanol. The resultingprecipitate was filtered to yield either of P25-P28.

Synthesis of P29

1-Bromo-5-(alkyl)thieno[3,4]pyrrole-4,6-dione (0.75 mmol),1-Bromo-5-(alkyl)thieno[3,4]pyrrole-4,6-dione (0.25 mmol),trans-di(μ-acetato)bis[o-(dio-tolyl-phosphino)benzyl]dipalladium(II) (4%mol), ligand (8% mol) and KOAc (1.00 mmol) were added in a Biotagemicrowave vial (size 2 to 5 mL) equipped with a magnetic stirring bar.The vial was sealed with a cap and then purged with nitrogen to removeany oxygen. THF (2 mL) was added and the reaction mixture was heatedusing an oil bath at 120° C. (reaction under pressure) for 22 h. Thereaction mixture was then cooled and the corresponding5-alkylthieno[3,4-c]pyrrole-4,6-dione (50 mg in 1 mL) was added as acapping agent. The solution was subsequently heated again at 120° C.over a period of 1 hour to complete the end-capping procedure. After anadditional hour of reaction time, the whole mixture was cooled to roomtemperature and poured into cold methanol (500 mL). The resultingprecipitate was filtered. Soxhlet extractions with acetone followed byhexanes removed catalytic residues and low molecular weight materials.Polymers were then extracted with chloroform. The solvent was reduced toabout 10 mL and the mixture was poured into cold methanol. The resultingprecipitate was filtered to yield P29.

Synthesis of P30

3,6-Bis(5-bromothiophen-2-yl)-2,5-bis(2-octyldodecyl)pyrrolo[3,4-c]pyrrole-1,4(2H,5H)-dione(101.9 mg, 0.1 mmol), 5-octylthieno[3,4-c]pyrrole-4,6-dione (26.5 mg,0.1 mmol), Pd(o-tol)(OAc) (1.9 mg, 4%),tris(ortho-methoxyphenyl)phosphine (2.8 mg, 8%), cesium carbonate (74.9mg, 0.23 mmol) and pivalic acid (3.1 mg, 0.03 mmol) were added in aBiotage microwave vial (5 mL) equipped with a magnetic stirring bar. Thevial was sealed with a cap and then purged with nitrogen to remove anyoxygen. Toluene (0.4 mL) was added and the reaction mixture was heatedusing an oil bath at 120° C. (reaction under pressure) for 24 h. Thereaction mixture was then cooled to room temperature and the polymerprecipitated by pouring the mixture into cold methanol/water (250/25mL). The precipitate was subsequently filtered. Soxhlet extractions withmethanol followed by hexanes removed catalytic residues and lowmolecular weight materials. Polymers were then extracted withchloroform. The solvent was reduced to about 10 mL and the mixture waspoured into cold methanol. P30 was obtained in 76% yield (M_(n) of 20.6kDa, M_(w)=36.1 kDa, PDI=1.8).

Synthesis of P31

3,6-Bis(5-bromothiophen-2-yl)-2,5-bis(2-octyldodecyl)pyrrolo[3,4-c]pyrrole-1,4(2H,5H)-dione(101.9 mg, 0.1 mmol), bis(5-octylthieno[3,4-c]pyrrole-4,6-dione) (52.9mg, 0.1 mmol), Pd(o-tol)(OAc) (1.9 mg, 4%),tris(ortho-methoxyphenyl)phosphine (2.8 mg, 8%), cesium carbonate (74.9mg, 0.23 mmol) and pivalic acid (3.1 mg, 0.03 mmol) were added in aBiotage microwave vial (5 mL) equipped with a magnetic stirring bar. Thevial was sealed with a cap and then purged with nitrogen to remove anyoxygen. Toluene (0.4 mL) was added and the reaction mixture was heatedusing an oil bath at 120° C. (reaction under pressure) for 48 h. Thereaction mixture was then cooled to room temperature and the polymerprecipitated by pouring the mixture into cold methanol/water (250/25mL). Soxhlet extractions with methanol followed by hexanes removedcatalytic residues and low molecular weight materials. Polymers werethen extracted with chloroform. The solvent was reduced to about 10 mLand the mixture was poured into cold methanol. P31 was obtained in 90%yield (M_(n) of 28.1 kDa, M_(w)=93.0 kDa, PDI=3.3).

Synthesis of P32

3,6-Bis(5-bromothiophen-2-yl)-2,5-bis(2-octyldodecyl)pyrrolo[3,4-c]pyrrole-1,4(2H,5H)-dione(101.9 mg, 0.1 mmol), 3,4-dicyanothiophene (13.4 mg, 0.1 mmol),Pd(o-tol)(OAc) (1.9 mg, 4%), tris(ortho-methoxyphenyl)phosphine (2.8 mg,8%), cesium carbonate (74.9 mg, 0.23 mmol) and pivalic acid (3.1 mg,0.03 mmol) were added in a Biotage microwave vial (5 mL) equipped with amagnetic stirring bar. The vial was sealed with a cap and then purgedwith nitrogen to remove any oxygen. Toluene (0.4 mL) was added and thereaction mixture was heated using an oil bath at 120° C. (reaction underpressure) for 48 h. The reaction mixture was then cooled to roomtemperature and the polymer precipitated by pouring the mixture intocold methanol/water (250/25 mL). Soxhlet extractions with methanolfollowed by hexanes removed catalytic residues and low molecular weightmaterials. Polymers were then extracted with chloroform. The solvent wasreduced to about 10 mL and the mixture was poured into cold methanol.P32 was obtained in 94% yield (M_(n) of 14.4 kDa, M_(w)=27.8 kDa,PDI=1.9).

Synthesis of P33

3,6-Bis(5-bromothiophen-2-yl)-2,5-bis(2-octyldodecyl)pyrrolo[3,4-c]pyrrole-1,4(2H,5H)-dione(101.9 mg, 0.1 mmol), 3,4-ethylenedioxythiophene (14.2 mg, 0.1 mmol),Pd(o-tol)(OAc) (1.9 mg, 4%), tris(ortho-methoxyphenyl)phosphine (2.8 mg,8%), cesium carbonate (74.9 mg, 0.23 mmol) and pivalic acid (3.1 mg,0.03 mmol) were added in a Biotage microwave vial (5 mL) equipped with amagnetic stirring bar. The vial was sealed with a cap and then purgedwith nitrogen to remove any oxygen. Toluene (0.4 mL) was added and thereaction mixture was heated using an oil bath at 120° C. (reaction underpressure) for 72 h. The reaction mixture was then cooled to roomtemperature and the polymer precipitated by pouring the mixture intocold methanol/water (250/25 mL). Soxhlet extractions with methanolfollowed by hexanes removed catalytic residues and low molecular weightmaterials. Polymers were then extracted with chloroform. The solvent wasreduced to about 10 mL and the mixture was poured into cold methanol.P33 was obtained in 52% yield (M_(n) of 5.1 kDa, M_(w)=6.5 kDa,PDI=1.3).

Synthesis of P34

Monomer 17 (61.2 mg, 0.15 mmol), monomer 28 (65.0 mg, 0.15 mmol),tris(ortho-methoxyphenyl)phosphine (4.2 mg, 0.012 mmol), cesiumcarbonate (117.3 mg, 0.36 mmol) and pivalic acid (6.1 mg, 0.06 mmol)were added in a Biotage microwave vial (5 mL) equipped with a magneticstirring bar. The vial was sealed with a cap and then purged withnitrogen to remove any oxygen. Toluene (0.75 mL) was added and thereaction mixture was heated using an oil bath at 120° C. (reaction underpressure) for 14 h. The reaction mixture was then cooled to roomtemperature, the crude reaction mixture dissolved in CHCl₃ and thepolymer precipitated in cold methanol/water (200/25 mL). Soxhletextractions with acetone followed by hexanes removed catalytic residuesand low molecular weight materials. Polymers were then extracted withchloroform. The solvent was reduced to about 20 mL and the mixture waspoured into cold methanol. P34 was obtained in 73% yield (M_(n) of 11.5kDa, M_(w)=30.2 kDa, PDI=2.63; UV-vis: (CHCl₃)

_(max)=512 nm, (solid)

_(max)=585, 628, 683 nm).

Synthesis of P35

Monomer 18 (105.8 mg, 0.17 mmol), monomer 23 (43.4 mg, 0.15 mmol),Pd(o-tol)(OAc) (4.8 mg, 0.0051 mmol), tris(ortho-methoxyphenyl)phosphine(6.7 mg, 0.019 mmol), cesium carbonate (149.9 mg, 0.46 mmol) and pivalicacid (6.9 mg, 0.068 mmol) were added in a Biotage microwave vial (5 mL)equipped with a magnetic stirring bar. The vial was sealed with a capand then purged with nitrogen to remove any oxygen. Toluene (0.85 mL)was added and the reaction mixture was heated using an oil bath at 120°C. (reaction under pressure) for 25 h. The reaction mixture was thencooled to room temperature, the crude reaction mixture dissolved inCHCl₃ and the polymer precipitated in cold methanol/water (200/50 mL).Soxhlet extractions with acetone followed by hexanes removed catalyticresidues and low molecular weight materials. Polymers were thenextracted with chloroform. The solvent was reduced to about 20 mL andthe mixture was poured into cold methanol. P35 was obtained in 70% yield(M_(n)=14.5 kDa, M_(w)=23.0 kDa, PDI=1.49; UV-vis: (CHCl₃) 526 nm,(solid)

_(max)=541 nm).

Synthesis of P36

Monomer 27 (93.2 mg, 0.15 mmol), monomer 23 (39.8 mg, 0.15 mmol),Pd(o-tol)(OAc) (3.8 mg, 0.004 mmol), tris(ortho-methoxyphenyl)phosphine(5.6 mg, 0.016 mmol), cesium carbonate (130 mg, 0.40 mmol) and pivalicacid (6.1 mg, 0.06 mmol) were added in a Biotage microwave vial (5 mL)equipped with a magnetic stirring bar. The vial was sealed with a capand then purged with nitrogen to remove any oxygen. Toluene (0.75 mL)was added and the reaction mixture was heated using an oil bath at 120°C. (reaction under pressure) for 15.5 h. The reaction mixture was thencooled to room temperature, the crude reaction mixture dissolved inCHCl₃ and the polymer precipitated in cold methanol/water (200/50 mL).Soxhlet extractions with acetone followed by hexanes removed catalyticresidues and low molecular weight materials. Polymers were thenextracted with chloroform. The solvent was reduced to about 20 mL andthe mixture was poured into cold methanol. P36 was obtained in 73%(M_(n)=14.0 kDa, M_(w)=32.4 kDa, PDI=2.3; UV-vis: (solid)

_(max)=620, 677 nm).

Synthesis of P37

5-Octyl-5H-thieno[3,4-c]pyrrole-4,6-dione (23) (53.1 mg, 0.2 mmol),6,6′-dibromo-N,N′-(2-hexyldecyl)-isoindigo (31) (173.8 mg, 0.20 mmol),trans-di(μ-acetato)bis[o-(di-o-tolyl-phosphino)benzyl]dipalladium(II)(9.4 mg, 2% mol), tris(o-methoxyphenyl)phosphine (14.1 mg, 8% mol) andCs₃CO₃ (130 mg, 0.40 mmol) were added in a Biotage microwave vial (5 mL)equipped with a magnetic stirring bar. The vial was sealed with a capand then purged with nitrogen to remove any oxygen. THF (1.0 mL) wasadded and the reaction mixture was heated using an oil bath at 120° C.(reaction under pressure) for 22 h. The reaction mixture was then cooledand the corresponding 5-alkylthieno[3,4-c]pyrrole-4,6-dione (50 mg in 1mL) was added as a capping agent. The solution was subsequently heatedagain at 120° C. over a period of 1 hour to complete the end-cappingprocedure. After an additional hour of reaction time, the whole mixturewas cooled to room temperature and poured into cold methanol (500 mL).The resulting precipitate was filtered. Soxhlet extractions with acetonefollowed by hexanes removed catalytic residues and low molecular weightmaterials. Polymers were then extracted with chloroform. The solvent wasreduced to about 10 mL and the mixture was poured into cold methanol.The resulting precipitate was filtered. P37 was obtained in 77% yield ofsoluble fraction in CHCl₃; M_(n) of 24.0 kDa and M_(w) of 52.9 kDa.

Synthesis of P38

5,5′-Dioctyl-4H,4′H-1,1′-bithieno[3,4-c]pyrrole-4,4′,6,6′(5H,5′H)-tetrone(24) (52.9 mg, 0.1 mmol), 6,6′-dibromo-N,N′-(2-hexyldecyl)-isoindigo(31) (86.9 mg, 0.10 mmol),trans-di(μ-acetato)bis[o-(di-o-tolyl-phosphino)benzyl]dipalladium(II)(1.9 mg, 2% mol), tri-tert-butylphosphonium tetrafluoroborate (2.3 mg,8% mol) and potassium acetate anhydrous (19.6 mg, 0.20 mmol) were addedin a Biotage microwave vial (size 2 to 5 mL) equipped with a magneticstirring bar. The vial was sealed with a cap and then purged withnitrogen to remove any oxygen. THF (0.5 mL) was added and the reactionmixture was heated using an oil bath at 120° C. (reaction underpressure) for 22 h. The reaction mixture was then cooled and thecorresponding5,5′-dioctyl-4H,4′H-1,1′-bithieno[3,4-c]pyrrole-4,4′,6,6′(5H,5′H)-tetrone(50 mg in 1 mL) was added as a capping agent. The solution wassubsequently heated again at 120° C. over a period of 1 hour to completethe end-capping procedure. After an additional hour of reaction time,the whole mixture was cooled to room temperature and poured into coldmethanol (300 mL). The resulting precipitate was filtered. Soxhletextractions with acetone followed by hexanes removed catalytic residuesand low molecular weight materials. Polymers were then extracted withchloroform. The solvent was reduced to about 5 mL and the mixture waspoured into cold methanol. The resulting precipitate was filtered. P38was obtained in 87% yield of soluble fraction in CHCl₃; M_(n) of 19.5kDa and M_(w) of 42.9 kDa.

Synthesis of P39

3,4-Ethylenedioxythiophene (26) (15.0 mg, 0.106 mmol),6,6′-dibromo-N,N′-(2-hexyldecyl)-isoindigo (31) (91.7 mg, 0.106 mmol),trans-di(μ-acetato)bis[o-(di-o-tolyl-phosphino)benzyl]dipalladium(II)(5.0 mg, 5% mol), tris(o-methoxyphenyl)phosphine (7.0 mg, 20% mol),pivalic acid (3.3 mg, 0.0317 mmol) and Cs₃CO₃ (79.6 mg, 0.243 mmol) wereadded in a Biotage microwave vial (size 2 to 5 mL) equipped with amagnetic stirring bar. The vial was sealed with a cap and then purgedwith nitrogen to remove any oxygen. Toluene (0.5 mL) was added and thereaction mixture was heated using an oil bath at 120° C. (reaction underpressure) for 24 h. The reaction mixture was then cooled and thecorresponding 3,4-ethylenedioxythiophene (50 mg in 1 mL) was added as acapping agent. The solution was subsequently heated again at 120° C.over a period of 1 hour to complete the end-capping procedure. After anadditional hour of reaction time, the whole mixture was cooled to roomtemperature and poured into cold methanol (300 mL). The resultingprecipitate was filtered. Soxhlet extractions with acetone followed byhexanes removed catalytic residues and low molecular weight materials.Polymers were then extracted with chloroform. The solvent was reduced toabout 5 mL and the mixture was poured into cold methanol. The resultingprecipitate was filtered. P39 was obtained in 44% yield of solublefraction in CHCl₃; M_(n) of 55.3 kDa and M_(w) of 95.2 kDa.

While the present disclosure has been described with reference to whatare presently considered to be the preferred examples, it is to beunderstood that the disclosure is not limited to the disclosed examples.To the contrary, the disclosure is intended to cover variousmodifications and equivalent arrangements included within the spirit andscope of the appended claims.

All publications, patents and patent applications are hereinincorporated by reference in their entirety to the same extent as ifeach individual publication, patent or patent application wasspecifically and individually indicated to be incorporated by referencein its entirety.

REFERENCES REFERRED TO IN THE SPECIFICATION

-   1. B. Carsten, F. He, H.-J. Son, T. Xu, L. Yu, Chem. Rev. 2011, 111,    1493-1528.-   2. Y.-J. Cheng, S.-H. Yan, C.-S. Hsu, Chem. Rev. 2009, 109,    5868-5923.-   3. a) G. P. McGlacken, L. M. Bateman, Chem. Soc. Rev. 2009, 38,    2447-2464; b) B. Legault, I. Petrov, S. I. Gorelsky, K. Fagnou, J.    Org. Chem. 2010, 75, 1047-1060; c) T. W. Lyons, M. S. Sanford, Chem.    Rev. 2010, 110, 1147-1169; d) L. Ackermann, R. Vicente, A. R. Kapdi,    Angew. Chem. Int. Ed. 2009, 48, 9792-9826; e) D. Alberico, M. E.    Scott, M. Lautens, Chem. Rev. 2007, 107, 174-238; f) O. René, K.    Fagnou, Adv. Synth. Catal. 2010, 352, 2116-2120; g) L. Chen, J.    Roger, C. Bruneau, P. H. Dixneuf, H. Doucet, Chem. Commun., 2011,    47, 1872-1874. h) M. Baghbanzadeh, C. Pilger, C. O. Kappe, J. Org.    Chem. 2011, 76, 8138-8142.-   4. a) L. Ackermann, Chem. Rev. 2011, 111, 1315-1345; b) O. René, K.    Fagnou, Org. Lett. 2010, 12, 2116-2119; c) T. Satoh, M. Miura, Chem.    Lett. 2007, 36, 200-205; d) B. Liégault, D. Lapointe, L. Caron, A.    Vlassova, K Fagnou, J. Org. Chem. 2009, 74, 1826-1834; e) M.    Lafrance, K. Fagnou, J. Am. Chem. Soc. 2006, 128,    16496-16497; f) J. J. Dong, J. Roger, C. Verrier, T. Martin, R. Le    Goff, C. Hoarau, H. Doucet, Green Chem. 2010, 12,    2053-2063; g) D. J. Schipper, K. Fagnou, Chem. Matter. 2011, 23,    1594-1600.-   5. a) Q. Wang, R. Takita, Y. Kikuzaki, F. Ozawa, J. Am. Chem. Soc.    2010, 132, 11420-11421; b) W. Lu, J. Kuwabara, T. Kanbara,    Macromolecules 2011, 44, 1252-1255; c) M. Sévignon, J. Papillon; E.    Schulz, M. Lemaire, Tetrahedron Lett. 1999, 40, 5873-5876.-   6. a) Y. Zou, A. Najari, P. Berrouard, S. Beaupre, B. R. Aich, Y.    Tao, M. Leclerc, J. Am. Chem. Soc. 2010, 132, 5330-5331; b) C.    Piliego, T. W. Holcombe, J. D. Douglas, C. H. Woo, P. M.    Beaujuge, J. M. J. Fréchet, J. Am. Chem. Soc. 2010, 132,    7595-7597; c) M.-S. Su, C.-Y. Kuo, M.-C. Yuan, U.-S. Jeng, C.-J. Su,    K.-H. Wei Adv. Mater. 2011, 23, 3315-3319; d) T.-Y. Chu, J. Lu, S    Beaupre, Y. Zhang, J.-R. Pouliot, S. Wakim, J. Zhou, M. Leclerc, Z.    Li, J Ding, Y. Tao J. Am. Chem. Soc. 2011, 133, 4250-4253; e) G.-Y.    Chen, Y.-H. Cheng, Y.-J. Chou, M.-S. Su, C.-M. Chen, K.-H. Wei,    Chem. Commun. 2011, 47, 5064-5066; f) D. Gendron, M. Leclerc, Energy    Environ. Sci. 2011, 4, 1225-1237; g) C. M. Amb, S. Chen, K. R.    Graham, J. Subbiah, C. E. Small, F. So, J. R. Reynolds, J. Am. Chem.    Soc. 2011, 133, 10062-10065; h) D. Gendron, P.-O. Morin, P.    Berrouard, N. Allard, B. R Aích, C. N. Garon, Y. Tao, M. Leclerc,    Macromolecules 2011, 44, 7188-7193.-   7. X. Guo, R. P. Ortiz, Y. Zheng, M.-G. Kim, S. Zhang, Y. Hu, G.    Lu, A. Facchetti, T. J. Marks. J. Am. Chem. Soc. 2011, 133,    13685-13697.-   8. a) G. Dyker, Angew. Chem. Int. Ed. 1999, 38, 1698-1712; b) V. S.    Thirunavukkarasu, K. Parthasarathy, C.-H. Cheng, Chem. Eur. J. 2010,    16, 1436-1440; c) F. Kakiuchi, S. Murai, Acc. Chem. Res. 2002, 35,    826-834.-   9. M.-C. Yuan, M.-Y. Chiu, S.-P. Liu, C.-M. Chen, K.-H. Wei,    Macromolecules 2010, 43, 6936-6938.-   10. M. Leclerc, F. M. Diaz, G. Wegner Makromol. Chem. 1989, 190,    3105-3116.

TABLE 1 Conditions for the Synthesis of P1 by Direct HeteroarylationPolycondensation Ligands Catalysts

P(t-Bu)₃HBF₄ 3 Pd(OAc)(o-Tol) 1 Pd(OAc)₂ 2 Entry % (Cat)/% (L) M_(n)^([b]) [kDa] PDI^([c]) DP R1^([a]) (P1) 2% (1)/8% (1) 56 2.6 80 R2^([a])(P1) 2% (1)/8% (2) —^(b) —^(b) —^(b) R3^([a]) (P1) 2% (1)/8% (3) —^(c)—^(c) —^(c) R4^([a]) (P1) 2% (2)/8% (1) 21 2.5 33 R5^([a]) (P1) 2.5%(2)/15% (1) —^(c) —^(c) —^(c) R6^([a]) (P1)  2.5% (2)/15% (1)^(d)  9 1.814  R7^([a]) (P1*) [e]  9 1.5 14 ^([a])P1 was synthesized by directheteroarylation cross coupling; ^([b])No polymerization reactionoccurred; ^([c])All the reaction product was recovered using acetoneSoxhlet extraction and no further characterization was performed onthese materials; ^([d])Reaction time was 44 hours instead of 22 hours;[e]P1* was synthesized by Stille cross-coupling.

TABLE 2 M_(n), M_(w) and I_(p) data for P5 M_(n) M_(w) Kg/mol Kg/molI_(p) Stille cross-coupling 32 89 2.8 Direct Arylation 32 109 3.4

TABLE 3 Optical and Electronic Properties of P9-P18 E_(g opt) HOMO (eV)LUMO (eV) E_(g cv) (onset) P9 (AP065) −5.56 −3.76 1.80 1.80 P10 (AP082)−5.56 −3.73 1.83 1.79 P11 (AP079) −5.66 −3.86 1.80 1.83 P12 (AP066)−5.57 −3.82 1.75 1.78 P13 (AP067) −5.60 −3.86 1.74 1.76 P14 (AP164)−5.67 −3.87 1.80 1.83 P15 (AP096) −5.66 −3.86 1.80 1.82 P16 (AP098)−5.66 −3.86 1.80 1.82 P17 (AP080) −5.96 −3.86 2.10 1.70 P18 (AP078)−5.95 −3.86 2.09 1.80

TABLE 4 Physical, Optical and Electronic Properties of P21 M_(n) M_(w)HOMO LUMO Eg^(elec) Eg^(opt) kg/mol kg/mol eV eV eV eV P21 (PB-465) 1215 −5.75 −3.95 1.8 1.77

TABLE 5 Physical and Thermal Properties of P22-P29 M_(n) (Kg/mol) PDI DPn^(a) T_(dec) ^(b) (° C.) P22 (P1) 23 1.5 53 53 420 P23 (P2) 22 1.4 5151 420 P24 (P3) 21 1.5 54 54 420 P25 (P4) 25 1.3 32 64 420 P26 (P5) 41.3 6 12 410 P27 (P6) 8 1.8 11 23 420 P28 (P7) 5 1.6 5 11 440 P29 (P8) 71.6 24 24 380 ^(a)number of TPD units; ^(b)evaluated by TGA at 5% massloss under nitrogen

TABLE 6 Spectroscopic and Electrochemical Properties of P22-29 in theSolid State I_(max) ^(a) I_(max) E_(g opt) E_(ox) ^(b) E_(red) ^(b)E_(g elect) (nm) (nm) (eV) (eV) (eV) (eV) P22 (P1) 523 539 1.9 1.5 −0.41.9 P23 (P2) 523 539 1.9 1.5 −0.4 1.9 P24 (P3) 481 481 2.2 1.7 −0.4 2.1P25 (P4) 481 481 2.2 1.7 −0.4 2.1 P26 (P5) 528 527 1.9 N.D.  N.D. N.DP27 (P6) 541 542 1.8 1.2 −0.4 1.6 P28 (P7) 523 533 1.8 1.2 N.D N.D P29(P8) 536 544 1.9 1.1 N.D N.D ^(a)Absorbance maxima done in CHCl₃solution; ^(b)onset of process potential

TABLE 7 Physical, Optical and Electronic Properties of P37-39 Mn Mw HOMOLUMO Eg^(elec) Eg^(opt) _(film) T_(deg) kg/mol kg/mol eV eV eV eV ° C.P37 24.0 52.9 −6.0 −4.2 1.8 1.72 412 P38 19.5 42.9 −6.1 −4.2 1.9 1.75420 P39 55.3 92.2 −5.4 −3.9 1.5 1.55 410

1-18. (canceled)
 19. A polymer comprising repeating units of theFormulae (V), (VI) or (VII):-[A¹-A²]-  (V);-[A³]-  (VI); or-[A³-A⁴]-  (VII), wherein A¹, A², A³ and A⁴ are independently selectedfrom aryl and heteroaryl; and the polymers were prepared using directarylation or heteroarylation conditions.
 20. The polymer of claim 19,wherein A¹, A², A³ and A⁴ are independently selected heteroaryl.
 21. Thepolymer of claim 20, wherein heteroaryl comprises at least one thienylgroup.
 22. The polymer of claim 21, wherein the at least one thienylgroup is fused to a 5-membered or 6-membered heterocyclo group.
 23. Thepolymer of claim 21, wherein the heteroaryl comprises a linear chain of2, 3 or 4 thienyl groups.
 24. The polymer of claim 20, whereinheteroaryl comprises an oxindole group, and indigo or isoindigo group.25. The polymer of claim 20, wherein A¹, A², A³ and A⁴ are independentlyselected from:

wherein R¹, R^(1′), R², R³, R⁴, R⁵, R⁶, R⁷, R⁸, R⁹, R¹⁰, R¹¹, R¹², R¹³,R¹⁴, R¹⁵, R¹⁶, R¹⁷, R¹⁸, R¹⁹, R²⁰, R²¹, R²², R²³, R²⁴, R²⁵, R²⁶, R²⁷,R²⁸, R²⁹ and R³⁰ are independently selected from H, CN and C₁₋₃₀alkyland

denotes the point of attachment with the adjacent “A” group.
 26. Thepolymer of claim 19, wherein at least one of A¹, A², A³ and A⁴ isindependently selected from phenyl, biphenyl, naphthyl and indanyl, inparticular, phenyl.
 27. The polymer of claim 19, characterized by havinga high molecular weight polymers and not comprising metals that are usedin alternative methods.
 28. The polymer of claim 27, selected from thegroup consisting of:

wherein n is the number of repeating units in the polymer chain. 29-30.(canceled)